On the Viscosities of Molten Slags. II : Viscosities of CaO-SiO_2-Al_2O_3-MgO Slags
スポンサーリンク
概要
- 論文の詳細を見る
In order to clarify the influence of MgO on the viscosity of blast furnace slag, viscosities of synthetic CaO-SiO_2-Al_2O_3-MgO slags were measured by the use of rotating inner-cylinder viscosimeter as in the case of the first report. Iso-viscosity lines at 1, 500 and 1, 600℃ are given in the diagrams. When MgO was added to CaO-SiO_2 slag, the viscosity decreased with increasing amounts of MgO up to about 20%, beyond which, however, it increased. The region of low viscosity in CaO-SiO_2-MgO slag was greater than that in CaO-SiO_2-Al_2O_3 slag. When MgO was added to CaO-SiO_2-Al_2O_3 slag, the viscosity decreased, moreover, change in viscosity at constant temperature caused by the change of slag composition became small, but these beneficial effects of MgO were less noticeable than those reported by McCaffery and coworkers. With respect to the fluxing quality, MgO has nearly the same or a little less influence in reducing the viscosity of slags comparing with that of CaO.
- 東北大学の論文
著者
関連論文
- Diffusion of Some Alloying Elements in Liquid Iron
- Rate of Desulphurization of Molten Iron by Slag under Reducing Condition
- On the Viscosities of Molten Slags. I : Viscosities of CaO-SiO_2-Al_2O_3 Slags
- On the Viscosities of Molten Slags. II : Viscosities of CaO-SiO_2-Al_2O_3-MgO Slags
- Activity of Chromium in Liquid Iron-Chromium System
- Rate of Desulphurization of Molten Iron by Slag under Reducing Condition. II : Influence of Silicon and Manganese
- Diffusion of Sulfur in Molten CaO-SiO_2-Al_2O_3 Slag
- Diffusion of Sulfur in Liquid Iron. II : Diffusion of Liquid Iron Saturated with Carbon
- Diffusion of Slufur in Liquid Iron. I : Diffusion in Pure Iron