高強度モルタルマトリックスの破壊パラメータに及ぼす短繊維の影響 : 高強度繊維補強コンクリート(HFRC)の破壊性状に関する研究
スポンサーリンク
概要
- 論文の詳細を見る
The influence of the short cut fiber on the fracture parameters of high strength mortar matrix was investigated in order to obtain a basic information on the fracture behavior of high-strength fiber reinforced concrete(HFRC). Three-point bending tests on pre-notched mortar beam specimens which containing short cut fibers were performed. Various kinds of short cut fibers were used for the specimens. Fracture parameters of the specimens were analyzed based on the poly-linear approximation analysis of the tension softening diagram with the data of a load-load point displacement curve. As the results, the use of short cut fibers was significant on the improvement of the toughness of high-strength mortar, and the appropriate fiber which improving the toughness of high-strength mortar was clarified. The fracture parameter proposed in the paper, such as toughness modulus(T.M.) , R-curve, was effective on estimating the toughness of fiber reinforced cementitious composites.
- 社団法人日本建築学会の論文
- 1997-07-30
著者
関連論文
- 高強度コンクリートのクリープ・乾燥収縮実験
- 1317 鉄筋コンクリートの収縮ひび割れ特性 : その1 自己収縮,乾燥収縮,圧縮クリープ(収縮・クリープ(4),材料施工)
- 1318 鉄筋コンクリートの収縮ひび割れ特性 : その2 乾燥収縮ひび割れ試験(収縮・クリープ(4),材料施工)
- 約5年間の実測データに基づくコンクリートのクリープ・収縮寸法効果の評価とクリープ予測方法の提案
- 約5年間のクリープ・収縮ひずみ測定データに基づく部材寸法の影響評価
- 1301 コンクリートの乾燥収縮ひびわれに関する実験的研究 : 鉄筋のひびわれ幅制御効果
- 1308 コンクリートの乾燥収縮時のAE特性に関する研究 : その2. 鉄筋引き抜け時のAE特性
- 1202 コンクリートの乾燥収縮時のAE特性に関する研究
- 1091 コンクリートのアコースティック・エミッションに関する研究 : RC梁の静的交番繰返し載荷時のAE
- 1091 コンクリート打設後の温度測定結果に基づく2,3の考察 : その2 初期水和熱による温度ひび割れ発生有無の検討結果