Formation of α Form Nylon 12 under High Pressure
スポンサーリンク
概要
- 論文の詳細を見る
The formation conditions of α form Nylon 12 under high pressure from the melt and from the quenched state were investigated by means of high-pressure differential thermal analysis and wide-angle X-ray diffraction. The α form was formed by crystallization from the melt above 200 MPa, and the γ form disappeared in the sample obtained above 500 MPa. The quenched state was transformed into the α form at lower temperature than the melting point of the α form under high pressure, whereas the γ form was hardly transformed at all. The thermal behavior of the α form at atmospheric pressure was also studied. Two endotherms due to the meltings of the α and γ forms and one exotherm due to the α to γ form transformation were observed. This transformation occurred without melting of the α form at a slow heating rate and was regarded as a monotropic transition.
- 社団法人応用物理学会の論文
- 1982-04-20
著者
-
Hiramatsu Nobuyasu
Department Of Applied Physics Faculty Of Engineering Kyushu University
-
HASHIDA Shigesou
Department of Applied Physics, Faculty of Science, Fukuoka University
-
HIRAKAWA Susumu
Department of Applied Physics, Faculty of Science, Fukuoka University
-
Hirakawa Susumu
Department Of Applied Physics Faculty Of Science Fukuoka University
-
Hashida Shigesou
Department Of Applied Physics Faculty Of Science Fukuoka University
関連論文
- Structure Investigation of Metal Ions Clustering in Dehydrated Gel Using X-ray Anomalous Dispersion Effect
- Structure Investigation of Metal Ions Clustering in Dehydrated Gel Using X-ray Anomalous Dispersion Effect
- Frequency Dispersion in Elastic Property During the Glass Transition of Dehydrated Polyacrylamide Gel
- Microphase Separation in Dehydrated N-isopropylacrylamide/sodium Acrylate Gel
- Elastic Anomaly and Glass Transition in Dehydrated Egg White Gel
- Difference in Low Frequency Raman Spectra between Dehydrated Egg White and the Dehydrated Heat-Treated Gel
- Change in the Low-Lying Raman Scattering Spectrum in the Glass Transition of Dehydrated Polyacrylamide Gel
- Raman Peak in Low-Frequency Region of Dehydrated Egg-White Gel
- Raman Scattering Study during the Dehydration Process of Polyacrylamide Gel
- Investigations of Pressure and Temperature Effects on Gelation Process of Egg White by Time-Resolved Turbidimetric Measurements
- Small-Angle Neutron Scattering Observation of Aqueous Suspension of Microcrystalline Cellulose
- Some Features in Gel Drying Process and Dehydrated Substances
- An X-Ray Color TV System with Preferred Display of Soft X Rays
- Ultrasonic Spectroscopy for Teflon/Glass Bead Composite System : Physical Acoustics
- Material Characterization of Polymeric Materials by Ultrasonic Spectroscopy : Physical Acoustics
- High Temperature Cell Using Polymide Buffer for Ultrasonic Spectroscopy : Medical Ultrasonics and Ultrasonic Measurements
- Formation of α Form Nylon 12 under High Pressure
- Mechanical Anisotropy in Oriented Nylon 12
- Pressure Dependence of Transitions and Relaxations in Polytetrafluoroethylene
- Study of Transformations among α, γ and γ' Forms in Nylon 12 by X-Ray and DSC
- Determination of Unit Cell for α-Form Nylon 12