Correlation between Adhesion Strength of Plasma-Polymerized Hexamethyldisiloxane Films to Polytetrafluoroethylene and Partial Discharge Resistance
スポンサーリンク
概要
- 論文の詳細を見る
Polytetrafluoroethylene (PTFE) films were coated with plasma-polymerized hexamethyldisiloxane (PPHMDS) films in a do glow discharge system. The correlation between the adhesion of the PPHMDS films to the PTFE films and the partial discharge resistance of the composite films was investigated. The voltage endurance of the composite films in the presence of partial discharges increased with the adhesion of the PPHMDS films. From an observation of the deteriorated surface scars, it was shown that the deterioration is affected by the formation of cracks in the PPHMDS film.
- 社団法人応用物理学会の論文
- 1995-09-15
著者
-
Aozasa Masao
Department Of Electrical Engineering Faculty Of Engineering Osaka City University
-
Kusabiraki Minoru
Department Of Electrical Engineering Faculty Of Engineering Osaka City University
関連論文
- Effects of perylene concentration on luminous characteristics of poly (N-vinylcarbazole) based organic EL device
- Photoluminescence of ZnS:Mn thin-film EL device active layer : influence of H2 gas in sputtering atomsphere
- Application of plasma-polymerized p-xylene thin film to organic EL device
- Effects of H2 gas in sputtering ambient on pulse voltage response of ZnS:Mn electroluminescent device
- Effects of evaporation condition on luminous characteristics of a single layer EL device
- Organic thin film EL device with plasma-polymerized N-ethylcarbazole as hole transport layer
- Optical emission spectroscopy of rf-magnetron sputtering plasma for fabrication of ZnS:Mn active layer in thin-film EL devices
- Effect of Electrode on the Electrical Conduction in Polyethylene under Micro-second Pulse Condition
- CaS:Eu, F Thin Film Electroluminescent Devices Prepared by RF Sputtering with Hydrogen-Argon Mixture Gas
- Diffusion of ZnS : Mn active layer to plasma polmerized p-xylene thin film
- Mn centers in Zns : Mn thin-film EL device active layer
- Correlation between Adhesion Strength of Plasma-Polymerized Hexamethyldisiloxane Films to Polytetrafluoroethylene and Partial Discharge Resistance
- Surface Modification of Polytetrafluoroethylene Films by Discharges
- Diffusion of ZnS : Mn active layer to plasma polmerized p-xylene thin film
- Mn^2^+ centers in Zns:Mn thin-film EL device active layer
- Infrared Observations of Polyethylene under the Condition of Electric Field Application