Diffusion of Zinc into GaAs

スポンサーリンク

概要

• 論文の詳細を見る

• Experimental studies have been made of the zinc diffusion into GaAs Crystals containing dislocations of 0 to 10^8 cm^<-2> at various arsenic vapor pressures. The diffused layers were observed by means of chemical etching and an infrared microscope. For the diffusion without arsenic, (1) the fast diffusion takes place in the presence of dislocations, and (2) a large number of dislocations, proportional to the square of the zinc concentration, are induced in the diffused layers. For the diffusion under high arsenic vapor pressure, (3) generation of new dislocations is suppressed in the shallow diffusion layers, while in layer deeper than 40∼60 μ the dislocation density is suddenly increased, accompanied by fast diffusion, thereby resulting doubly stepped diffusion front, (4) the rate of the ordinary substitutional diffusion is comparatively lowered, and (5) the existence of ZnAs_2 is detected in the diffused layer. The observed fast diffusion along the dislocations is qualitatively interpreted in terms of an induced dislocation model.

• 社団法人応用物理学会の論文
• 1968-05-05

著者

• Maruyama Mitsuhiro

  Central Research Laboratories Nippon Electric Company Limited

関連論文

• Improvement of the Interface Impurity Profile of Vapor Grown GaAs by Using Doubly Doped Substrate
• Diffusion of Zinc into GaAs
• Ruby Crystals Grown by the Czochralski Technique

スポンサーリンク