Electron Diffraction at Low Temperature IV. : Amorphous Films of Iron and Chromium Prepared by Low Temperature Condensation
スポンサーリンク
概要
- 論文の詳細を見る
Films of iron and chromium were prepared at 4.2°K which show diffuse halo electron diffraction patterns characteristic of an amorphous state. In order to decide whether these films are in an amorphous state or consist of very fine crystallites, the radial distribution analysis was carried out for them. The results of analysis lead to the conclusion that the state of atomic aggregate of these films is certainly amorphous.
- 社団法人応用物理学会の論文
- 1966-11-15
著者
-
Fujime Satoru
The Research Institute For Iron Steel And Other Metals
-
Fujime Satoru
The Research Lnstitute For Iron Steel And Other Metals Tokyo University
関連論文
- The Intensity of Satellite Reflections in Electron Diffraction Patterns from Evaporated Alloy Films with CuAu II Type Superstructure
- The Intensity of Satellite Reflections in Electron Diffraction Patterns from Evaporated Alloy Films with CuAu II Type Superstructure
- Electron Diffraction at Low Temperature : I. Apparatus and Preliminary Results
- Supplement to "Electron Diffraction at Low Temperature" Radial Distribution Analysis of a Film Composed of Very Fine Crystallites
- Electron Diffraction at Low Temperature IV. : Amorphous Films of Iron and Chromium Prepared by Low Temperature Condensation
- On an Amorphous Au-Co Alloy Film
- Electron Diffraction at Low Temperature IV. : Amorphous Films of Iron and Chromium Prepared by Low Temperature Condensation
- On the {00.1} Spots in Electron Diffraction Patterns from the Precipitates of an Al-20% Ag Alloy
- On Forbidden Reflection Spots and Unexpected Streaks Appearing in Electron Diffraction Patterns from Hexagonal Cobalt
- On the {00.1} Spots in Electron Diffraction Patterns from the Precipitates of an Al-20%Ag Alloy
- Electron Diffraction at Low Temperature II. : Radial Distribution Analysis of Metastable Structure of Metal Films Prepared by Low Temperature Condensation
- On Forbidden Reflection Spots and Unexpected Streaks Appearing in Electron Diffraction Patterns from Hexagonal Cobalt
- Electron Diffraction at Low Temperature II. Radial Distribution Analysis of Metastable Structure of Metal Films Prepa ed by Low Temperature Condensation
- On an Amorphous Ag-Cu Alloy Film
- Electron Diffraction at Low Temperature. V. : On Amorphous Films of Transition Metals and Alloys Prepared by Low Temperature Condensation
- Electron Diffraction at Low Temperature III. : Radial Distribution Analysis of Metastable Structure of Metal Films Prepared by Low Temperature Condensation
- Electron Diffraction at Low Temperature : V. On Amorphous Films of Transition Metals and Alloys Prepared by Low Temperature Condensation