塑性拘束が脆性破壊発生におよぼす影響と軟質溶接継手の脆性破壊強度に関する研究

概要

論文の詳細を見る
In the soft welded joints having notches in the weld metal, plastic deformation at the notch tip will be held in check by the stronger base metals. In the present report, effect of plastic constraint caused due to mechanical heterogeneity on brittle fracture initiation is investigated. Notched wide plate with groove tensile tests (Groove Deep Notch Test) were carried out as a clue to elucidate effects of plastic constraint on plastic behaviors at crack tip and critical crack opening displacement, and deep notch test of soft welded joints which have saw cut notches in weld metal was carried out. The main results obtained are summarized as follows : (1) As the plastic constraint factor becomes larger, the applied stress required to produce a constant crack opening displacement becomes larger (Fig.9) and the critical crack opening displacement Φ_c becomes smaller (Fig.10). The brittle fracture net stress is maximum at a certain value of plastic constraint factor (Figs. 3,11). (2) The relations between the applied stress and crack opening displacement for various values of plastic constraint factor can be calculated by considering increase of the general yield stress due to plastic constraint (Figs. 9,16). (3) In the practical soft welded joints, the brittle fracture strength is affected more considerably with fracture toughness than yield strength of weld metal.
社団法人日本船舶海洋工学会の論文