工業用純Ti/純Alの摩擦圧接継手の特性におよぼす後熱処理の影響 : Ti系/Al系材料の摩擦圧接に関する研究(第1報)

概要

論文の詳細を見る
In this report, the friction welding conditions for commercially pure titanium/pure aluminium joint were developed, and the effect of post-weld heat treatment (PWHT) on the mechanical and metallurgical properties of the complete friction welds was examined in basic research. The friction welding conditions range, which can produce the complete weld joints having more than 100% joint efficiency as joint tensile property and excellent bend ductility in the as-welded conditions, was clarified. PWHT temperatures including up to 873 K (600℃) for 36 ks (1 H) had no influence on joint mechanical properties, especially, joint tensile and bend ductility. However, they drastically decreased during PWHT at 873 K (600℃) for more than 72 ks (20 H). X-ray diffraction analysis and SEM observation confirmed that those reductions were due to the formation of large contents of Al_3Ti intermetallic compound phase at the pure titanium/pure aluminium interface. The critical width of Al_3Ti phase (at PWHT of 873 K for 72 ks), which steeply reduced the mechanical properties, was around 10 μm. Several atomic percents of silicon concentrated in the Al_3Ti phase.
社団法人溶接学会の論文
1994-02-05