接合界面におけるめっき層の組織と接合性に及ぼすめっき浴組成の影響 : マイクロパラレルシーム接合法とその接合機器の開発(第3報)
スポンサーリンク
概要
- 論文の詳細を見る
Experimental evaluation of hermeticity and joining strength and an investigation of joints by SEM, EPMA, AES, were accomplished on hermetically sealed package by Micro-Parallel Seam Joining (MPSJ) using a lid (Fe-Ni-Co alloy) normally applied as hermetic seal of ceramic package for highly reliable LSI, nickel plated in both Watts Bath and Sulfamate Bath. The results are summarized as follows.(1) Crack was observed at the grain boundary in a plating layer at the joining interface of ceramic package which was hermetically sealed with use of nickle plated lid in a Sulfamate Bath. The crack is considered to be caused by sulfur segregation at the grain boundary from the result of investigation by SEM and AES. As a result, both hermeticity and joining strength were unsatisfactory.(2) Tendency of crack occurrence was observed to be especially notable at the seam joint after thermal cycling test performed to evaluate reliability of joint rather than immediately after joining. Therefore, thermal cycling test is considered to be an effective means for evaluation of crack occurrence.(3) Crack was not observed at the joining interface of hermetically sealed package using nickel plated lid in a Watts Bath and indicated to be a sound joint structure. Both hermeticity and joining strength were resulted to be satisfactory. However, peeling of plated layer at an area of the lid slightly away from the joining section was observed on a lid applied with thick plating of 10μm. Therefore, plating thickness of approximately 3.5μm in a Watts Bath is considered to be adequate.(4) Correlation between hermeticity and peel strength was not found on package hermetically sealed with use of nickel plated lid in a Sulfamate Bath. Although specified value for hermeticity was satisfied, peel strength was zero or a value close to zero on some specimens. Therefore, both methods are required to be performed as an evaluation method for joint of hermetically sealed package by MPSJ method.
- 1988-11-05
著者
関連論文
- マイクロ抵抗溶接の機器と接合事例 (特集 マイクロ接合の適用と現状)
- 310 適応制御抵抗スポット溶接システムの自動車部品製造への適用
- 接合界面におけるめっき層の組織と接合性に及ぼすめっき浴組成の影響 : マイクロパラレルシーム接合法とその接合機器の開発(第3報)
- 新しいマイクロパラレルシーム接合装置の開発とその応用 : マイクロパラレルシーム接合法とその接合機器の開発(第4報)
- 電子部品の接続技術分科会報告
- 抵抗溶接法と超音波溶接法を利用した被覆細線の溶接技術
- セラミックパッケージの表面温度とシーム接合条件 : マイクロパラレルシーム接合法とその接合機器の開発(第2報)
- リフロー・ソルダリングにおけるインプロセス・モニタリングと制御 (フォーラム「溶接品質のインプロセス制御」)
- 接合界面におけるめっき層の存在と接合性への影響 : マイクロパラレルシーム接合法及び接合機器の開発(第1報)
- 333 マイクロパラレルシーム接合法とその機器の開発(第4報) : パッケージの表面温度とシーム接合条件との関係について
- 314 マイクロ・パラレル・シーム接合法と機器の開発(第2報) : 接合過程中におけるパッケージ表面温度分布の測定
- 313 マイクロ・パラレル・シーム接合法と機器の開発(第1報)
- 材料・装置--瞬間加熱式リフロソルダリング装置 (マイクロ接合技術--IC、LSIを対象にした実践ガイド) -- (ソルダリング編)
- マイクロエレクトロニクスと接合技術 (マイクロ接合技術--IC、LSIを対象にした実践ガイド)
- 新しいはんだ付装置-リフロソルダリング装置を中心に (高信頼度はんだ付け--実践のためのガイドブック)
- マイクロソルダリング装置--装置の概要と応用 (はんだ付け技術実践ガイドブック) -- (装置の選定と使用法)
- 集積回路製造における接合技術
- エレクトロニクス分野におけるはんだ付け法--リフロソルダリング技術とその応用 (最新ろう接技術と装置・材料)
- 電子部品の組立, 実装と抵抗溶接
- 448 適応制御システムによる抵抗スポット溶接部の品質保証特性
- 149 適応制御抵抗スポット溶接裝置