共晶反応を利用したアルミニウムパイプと銅パイプの圧接 : Al部材の圧接に関する研究(第一報)
スポンサーリンク
概要
- 論文の詳細を見る
A new pressure joining method has been developed for transition joints between aluminum and copper pipes. The joining procedure is characterized by the following steps. 1) The ends of aluminum and copper pipes are set into contact with each other under a initial pressure that does not result in plastic deformation of the pipes. 2) The pipes are rapidly heated by an induction mtehod up to a temperature just above the eutectic temperature. 3) After an adequate quantity of eutetic liquid is formed, a second pressure, which is highre than the initial pressure, is applied to exclude the eutectic liquid out of the interface. Changes in the length of aluminum and copper pipe are detected to estimate the quantity of eutectic liquid. When the length changes by a predetermined value, the heating is terminated to cool the joint and the second pressure is applied. Many pipes of diameter 8 mm were joined in a protective gas atmosphere under various condition for the amount of eutectic liquid and the second pressure. The joints were evaluated by a metallographic examination, mechanical tests and leak tests. The residual eutectic layer at the joining interface becomes thinner with increasing second pressure. Joints with a layer less than 0.1 μm in thickness were obtained at a pressure of 30 MPa. Joints with such thin layers never break down at the joining interface during repeated bending fracture tests, but the aluminum pipes break down outside the interface. The leak rate of helium in the joints with thin residual eutectic layers is less than 1×10^<-13>Pa m^3/s even after joints were subjected to repeated bendings, thermal cycles and flattening deformations.
- 社団法人溶接学会の論文
- 1988-11-05
著者
関連論文
- 粗大Cr炭化物を分散したNi合金の高温水中での耐摩耗性
- コバルトフリー材の耐摩耗性に及ぼす炭化物の分散効果
- 共晶反応を用いたアルミニウムの圧接 : Al部材の圧接に関する研究(第2報)
- 共晶反応を利用したアルミニウムパイプと銅パイプの圧接 : Al部材の圧接に関する研究(第一報)
- アルミニウム部材の高速圧接法の開発
- 共晶反応を利用したアルミニウム接合法の開発 (材料)
- 441 共晶反応を利用したAl-Cuパイプ圧接法の開発
- 連載「21世紀の塑性加工に何が求められるか」III : 21世紀の地球環境と塑性加工
- 101 低入熱領域におけるTIG及びレーザ溶接の熱効率・溶融効率の検討
- 111 高周波パルスTIGを用いた狭開先溶接の研究
- SiCとCu-Mn合金との界面反応 : セラミックスと金属との接合に関する研究(第2報)
- Cu-Mn液相インサート材を用いたSiCとCuとの反応接合 : セラミックスと金属との接合に関する研究(第一報)
- SiCセラミックスと銅との接合及びその接合体の熱的特性 : セラミックスと金属との接合(第1報)
- 13・8 回転成形・管成形 : 13. 塑性加工