Cr-Mо鋼の再熱割れの発生時期について : Cr-Mo鋼の再熱割れに関する研究, 第5報(昭和59年度春季全国大会論文発表講演論文)

概要

論文の詳細を見る
The crack initiating temperature and time of reheat cracking were investigated on three types of commercial heat resistnig steels. Two modified implant test machines were employed, one of which was constant strain type (stress relaxation type) and the other was constant load type. The crack initiating curves for those steels were drawn on the stress-temperature (time) diagrams. The results were summerized as follows.(1) The crack initiating temperatures obtained by the constant strain test were 550,510 and 540℃ for 1/2Mo, 1Cr-1/2Mo and 21/4Cr-1Mo steels, respectively, when the stress was high enough (σ_<PW>>30 kg/mm^2). The crack initiating temperature elevated with the decrease of the stress.(2) The crack initiating temperatures obtained by constant load test agreed with those by constant strain test, only when the stress was high. The crack initiating curves of the former situated generally in higher stress-and longer duration side than that of the latter. This difference will come from the difference of the stress during the preparation stage prior to crack initiation.(3) The crack initiating temperature was not so much varied by the variation of Cr and Mo contents of a very wide range.
社団法人溶接学会の論文
1984-02-05