Cr-Mo鋼熱影響部におけるSR処理温度付近の焼もどし脆化 : Cr-Mo鋼熱影響部の焼もどし脆化に関する研究(第3報)

概要

論文の詳細を見る
The temper embrittlement of the high-temperature type arises in the heat affected zones (HAZs) when the welded constructions of Cr-Mo steels were subjected to the stress-relief (SR) heat treatment in the temperature range above 900 K. In the temperature range below 900 K, there arose four types (the first to the fourth types) of temper emgrittlement as shown by the authors in the previous papers. The temper embrittlement of the high-temperature type (the fifth type) arising in 2 1/4Cr-1Mo and 1 1/4Cr-1/2Mo steels was examined in this research in connection with those four types. Charpy impact test was made on the synthetic HAZ specimens tempered at 900 K to 1000 K. Experimental results informed that 2 1/4Cr-1Mo steel in possiblly embrittled by SR treatment, because the SR temperature of this steel (about 975 K) meets that at which the fifth type arises. Shorter holding time is recommended for avoiding the embrittlement. 1 1/4Cr-1/2Mo steel is more possiblly suffered from the third type rather than the fifth type, because the SR temperature of this steel (about 925 K) meets that in which the third type arises. The role of carbide particles of inducing the fifth type of embrittlement was discussed in some detail.
社団法人溶接学会の論文
1997-08-05