100 キロ高張力鋼多層溶接継手の割れ試験結果 : 大形 TRC 試験に関する研究(第 1 報)

概要

論文の詳細を見る
The present study is an application of the NRIM TRC test (Tensile Restraint Cracking test) to cold cracking in multilayer welds of a high-sterngth steel with a strength level of 100kg/(mm)^2. It was aimed in this study to make clear the cracking behavior and to get practical methods for the prevention of cracking. A TRC specimen was set up in a 1000 tons NRIM TRC tester and pulled after finishing of a test weld. The constant loading at various stress levels was sustained for sufficient time for cracking. There occurred two types of macrocracks in multilayer welds depending on the dircetion of restraining, that is, transverse and longitudinal cracks in longitudinal and transverse TRC tests, respectively. Those cracks in longitudinal and transverse TRC tests, respectively. Those cracks were considered extensions of microcracks. Cracks, both transverse and longitudinal, were the delayed type due to hydrogen and occurred after an incubation period nnder a sustained tensile loading which exceeded the critical tensile stress for cracking. The incubation period extended from about 1 to 10hr, mainly depending on restraining stress and hydrogen content. The critical tensile stress for cracking was raised with an increase of preheating temperature and with a decrease of hydrogen content. The critical tensile stress for longitudinal cracking was slightly lower than that for transverse cracking at the same welding conditions and hydrogen content. Transverse cracks were prevented under the longitudinal tensile stress of 65kg/(mm)^2 with any of the following methods : (a) preheating at 200℃, (b) 100℃ preheating and locally tempering postheating at 500℃, or (c) 150℃ preheating and lower temperature postheating for 5hr at 100℃. The restraining stress of 65kg/(mm)^2 was a little over the restraining stress in the so-called window restrained test which has been appreciated as fairly reporducible one of actual severe restraint. Very little change of hydrogen content, about 0.2cc/100g, in deposited metal was decisive to transverse cracking in such high strength steel welds, supposing acturl joints with severe restraint. Longitudinal cracks were gradually propagated and then usually caused a brittle fracture throughout the joint. The carck was prevented with preheating at 200℃ under the transverse tensile stress of 55kg/(mm)^2 At the tensile stress of 65kg/(mm)^2 any crack did not occur with simultaneous use of 150℃ preheating and lower temperature postheating, 200℃ for 1hr or 100℃ for 5hr. Effectiveness of lower temperature postheating was discussed with an estimation of existing hydrogen content in a weld at the instant of cracking.
社団法人溶接学会の論文
1968-11-25

100 キロ高張力鋼多層溶接継手の割れ試験結果 : 大形 TRC 試験に関する研究(第 1 報)

スポンサーリンク

概要

著者

関連論文

スポンサーリンク