SM50B 突合せ溶接継手における疲労き裂伝播しきい値に及ぼす引張残留応力の影響

概要

論文の詳細を見る
The fatigue crack propagation rate and the stress intensity threshold level were measured on welded joints which were made by three kinds of welding processes, manual arc welding with covered electrode, gas metal arc welding, and submarged arc welding. The specimens were 200mm wide center notched type. The material was a SM50B steel 20mm in thickness. The fatigue crack propagation properties of the weld metal and the heat affected zone of these welded joints were found to be quite similar to each other and inferior to that of the base metal. The stress intensity threshold level of welded joints was about one fourth of that of the base metal. It is assumed that the inferiority of welded joints in crack propagation properties may be caused from the tensile residual stresses distributed in the middle part of the specimens. The removal of the tensile residual stresses by postweld heat treatment could improve welded joints in the fatigue crack propagation properties. The fatigue crack propagation properties and the stress intensity threshold level of welded joints after the postweld heat treatment are similar to those of the base metal.
社団法人溶接学会の論文
1981-02-05