TIG 溶接用タングステン電極の性質 : 電流容量および消耗
スポンサーリンク
概要
- 論文の詳細を見る
In this paper, the author intends to determine the current capacity and consumption of tungsten electrode in TIG arc welding for the purpose of establishing the standard (JIS) of the electrode. From this work, the following conclusions are obtained : (1) The current capacity of pure tungsten electrode under DCSP depends on Joule's heat and consequently on the stick-out length of electrode, and is formulated by experiment as I_m=220×(α/le×(10)^2)^<3/4>, where a is the cross section of electrode in (cm)^2 and le is the stick-out length of electrode in cm. The current capacity of thoriated tungsten in argon shielded DCSP arc is rather a little less than that of pure tungsten. (2) The DCRP current capacity has not a definite critical value, but is determined from a practial standpoint. (3) The failure of electrode due to over current in the AC TIG arc occurs in two ways; that is, of S. P. type in smaller diameter electrode and of R. P. type in larger diameter electrode. The AC capacity depends largely on the amount of DC component, and their relation is given by I_m=I_<m0>/(1-αPd), where I_<m0> is the maximum allowable current in the case of balanced AC, Pd is the ratio of DC component to effective value of AC component and α is a theoretically given coefficient. The AC capacity of thoriated tungsten is considerably larger than that of pure tungsten. (4) From careful measurements using water-cooled Cu anode or aluminum plate as a work piece and preventing start spattering, the electrode consumption under DCSP steady arc is found to be a few mg/30min. and seems to be caused through pure evaporation. The electrode consumption for AC arc under the same condition is 2 to 3 times the value mentioned above. (5) For the arc when using steel plate as base electrode, the consumption is nearly 10 times that for DCSP arc with water cooled Cu anode, and especially in the case of the AC arc successive spattering sometimes accompanies. (6) At the start of DCSP arc, the spattering of electrode is caused when applying nearly maximum allowable current suddenly to pure tungsten which was once used. Start spattering is not caused by (a) thoriated tungsten (b) pure, virgin tungsten, (c) arc starting with smaller current. (7) The start spattering is found to occur succeedingly for about 1/4sec. following the arc ignition, and seems to be caused by the cavity formed at the tip of electrode and the thermal shock.
- 社団法人溶接学会の論文
- 1963-10-25
著者
関連論文
- (16) 高マンガン鋼のガスシールドアーク溶接 (4) : 高マンガン鋼レールのエレクトロガス溶接
- 高マンガン鋼のガスシールドアーク溶接(第 1 報) : 溶接金属の性質におよぼすシールドガスおよび溶接条件の影響
- (112) 高マンガン鋼のガスシールドアーク溶接 (2) : 溶着鋼の性質におよぼす溶接条件の影響
- 高マンガン鋼のガスシールドアーク溶接(第 3 報) : 高マンガン鋼レールのエレクトロガス溶接
- 高マンガン鋼のガスシールドアーク溶接(第 2 報) : 再現熱影響部のじん性
- (24) ステンレス鋼板と軟鋼板とのアーク溶接 : 被覆アーク溶接およびティグ溶接による薄鋼板溶接部の性質(昭和 41 年度春季全国大会講演概要)
- (9) 高マンガン鋼のガスシールドアーク溶接 (3) : 再現熱影響部のじん性(昭和40年春季全国大会講演概要)
- (111) 高マンガン鋼のガスシールドアーク溶接 (1) : 高マンガン鋼用電極線によるガスシールドアークの特性
- 117 硬銅線の常温圧接の檢討(1)
- (72) アルミニウム合金のプラズマアーク切断 : 切断面の性状と溶接への影響
- アルミニウム合金の MIG スポット溶接法の改善 : 酸素ガスの混合が溶込みにおよぼす影響
- (104) アルミニウム合金の MIG アークスポット溶接法の改善について : 酸素ガスの混合が溶込みにおよぼす影響
- アルミニウム合金の溶接 : 溶接金属の性質および溶接欠陥を中心とする冶金的な問題点(非鉄材料の溶接)
- (96) 交流ティグ溶接の直流分について
- 熔接におけるタングステンアークの理論と研究の展望 (3)
- 熔接におけるタングステンアークの理論と研究の展望 (1)
- 243 硬銅線の突合せ常温圧接(第2報) : 圧接部の軟化現象
- (30) Al・Zn・Mg 系 3 元合金の MIG アークスポット溶接
- (88) 高合金鋼ミグ溶接におけるワイヤ抵抗効果
- C. 非鉄金属のガスシールドアーク溶接(わが国における溶接法の研究ならびにその適用の現状)
- TIG 溶接用タングステン電極の性質 : 電流容量および消耗
- Al鋳物合金の溶接性(第2報) : 主として逆曲げ溶接亀裂試験
- (102) TIG 溶接におけるタングステン電極の性質(昭和 37 年度秋季全国大会講演概要)
- (75) Al 鋳物合金の溶接性 (2) : 主として逆曲げ溶接亀裂試験(昭和 37 年度春季学術講演会講演概要)
- MIGアークにおける芯線の熔融と熔滴の移行(その2) : ステンレススチール(308)線の熔融
- MIGアークにおける芯線の熔融と熔滴の移行 : その1
- (3) MIGアークにおける芯線の熔融と熔滴の移行(その2) : ステンレススチール(308)線の熔融(昭和32年度秋季学術講演会講演概要)
- MIG アークにおける芯線の熔融と熔滴の移行 (その1) : 昭和32年度春季学術講演会講演概要
- 車両用輕合金の MIG 熔接と熔着金属の二三の性質
- (1) 車輛用輕合金の MIG 熔接と熔着金属の二三の性質(熔接学会 30 周年記念講演概要)
- 軽合金の溶接技術の進歩発展に貢献した功績