アーク溶接過程における水素の挙動(第 2 報) : 被覆アーク溶接で母材へ拡散する水素の測定
スポンサーリンク
概要
- 論文の詳細を見る
It has widely been accepted that the hydrogen which diffuses from weld metal into base metal in the arc welding plays an important role in embrittlement and formation of delayed cracks in the heat affected zone of weldment, but the direct measurement of such hydrogen has scarecely been reported. This paper describes a new device has been used to determine the volume of hydrogen diffusing from weld metal into base metal as a function of time, and the effects of moisture in the coating of electrode, strength of steel and preheating temperature on the behavior of hydrogen diffusing into the heat affected zone are investigated. The mian results obtained are as follows; 1) By the use of a vacuum system, the technique can accurately estimate the hydrogen diffusing from weld metal into base metal for a comparatively simple device. 2) When electrode containing the same humidity is used, the hydrogen content in the heat affected zone of weldment decreases with increasing strength of steel. 3) The hydrogen content in the heat affected zone increases with the increase in preheating temperature, and the magnitude of increment decreases as steel increases its strength. 4) It is necessary to consider the chemical composition of base metal in the hydrogen test of weld metal, because about half of the diffusible hydrogen estimated by JIS method may be the hydrogen diffusing into base metal. 5) The behavior of hydrogen in the heat affected zone of weldment during and after the arc welding may be dealt with engineering parameter (D^^^-)^* proposed in this paper on an assumption of unidimensional diffusion of hydrogen.
- 社団法人溶接学会の論文
- 1973-04-25
著者
関連論文
- 酸素アセチレン焔に關する研究(第 2 報) : 酸素アセチレン焔の混合比におよぼす火口温度の影響
- 酸素アセチレン焔に関する研究(第 1 報) : 火口温度の上昇について
- アーク溶接過程における水素の挙動(第 3 報) : 被覆アーク溶接金属の拡散性水素源について
- 318 上向すみ肉溶接部に発生するトウ・クラックについて
- 厚板 HT-80 鋼のサブマージアーク溶接の研究(第 2 報) : 部分溶込みかど溶接継手に発生するわれについて
- 可変拘束度すみ肉溶接割れ試験について
- 210 すみ肉溶接部に発生する冷間割れについて(第二報) : 各種の割れにおよぼす拘束度の影響
- 209 すみ肉溶接部に発生する冷間割れについて(第一報) : 残留応力分布におよぼす拘束度の影響
- Acoustic Emission 法の溶接割れ検出への応用(第 1 報)(溶接金属の水素量)
- 121 Acoustic emission法による溶接部遅れ割れの研究(第一報)
- アーク溶接過程における水素の挙動(第 2 報) : 被覆アーク溶接で母材へ拡散する水素の測定
- 142 溶接過程での水素の挙動(第3報) : 溶接時に母材に拡散する水素量