アーク溶接過程における水素の挙動(第 3 報) : 被覆アーク溶接金属の拡散性水素源について
スポンサーリンク
概要
- 論文の詳細を見る
Studies are made to determine the sources of hydrogen in shielded metal arc weld metal. First, by assuming that dissolution of hydrogen in molten metal obeys Sieverts' law, an equation is theoretically derived which is able to distinguish between the effects of humidity in the ambient atmosphere and those of moisture from the electrode coating. Next, the coefficients involved in the equation are determined experimentally. Finally, a formula which can predict the diffusible hydrogen content in the weld metal of HT50-HT100 steels is proposed. The results are summarized as follows : 1) Evaporation of water from coating flux of low hydrogen type electrode occurs in two stages; one is the evaporation of moisture up to about 200℃ and the other is that of bound water with a peak temperature at 750℃. 2) The effects of slag covering and its basicity in weld puddle on the diffusible hydrogen content are negligible in the case of low hydrogen type electrode. 3) Moisture evaporated from the coating of electrode at elevated temperatures contributes as the cause of the diffusible hydrogen in weld metal much more than that evaporated at relatively low temperatures. 4) The diffusible hydrogen content [H]_D in weld metal in ml/100g is given by [H]_D=(A+12a+0.64b)^<1/2>-1.8,where A is a material constant of electrode which depends mainly on the evaporation of moisture at elvated temperatures in ml/100g, a being moisture content in the coating in wt.% and b the partial pressure of vapour in the ambient atmosphere in mmHg. 5) The above equation gives the practical information to control the diffusible hydrogen content in weld metal.
- 社団法人溶接学会の論文
- 1973-05-25
著者
関連論文
- 酸素アセチレン焔に關する研究(第 2 報) : 酸素アセチレン焔の混合比におよぼす火口温度の影響
- 酸素アセチレン焔に関する研究(第 1 報) : 火口温度の上昇について
- 363 ステンレス鋼の抵抗加熱時の昇温特性 : ステンレス鋼の高周波電縫溶接現象(第 1 報)(冷延薄板, 溶接鋼管, 加工・システム・利用技術, 日本鉄鋼協会第 109 回(春季)講演大会)
- 362 電縫鋼管におけるフッククラックの発生機構(冷延薄板, 溶接鋼管, 加工・システム・利用技術, 日本鉄鋼協会第 109 回(春季)講演大会)
- SUS316L鋼MIG溶接金属の低温靱性の改善(昭和59年度秋季全国大会論文発表講演討論記録)
- SUS316L鋼MIG溶接金属の低温靱性の改善(昭和59年度秋季全国大会論文発表講演論文)
- 133 極低温用SUS 316L MIG 溶接金属のじん性
- マグ溶接の欠陥と補修
- 739 溶射圧延表面被覆鋼板の溶接性および耐食性(遅れ破壊, 圧力容器, 腐食, 腐食割れ, 材料, 日本鉄鋼協会第 112 回(秋季)講演大会)
- 738 溶射圧延法による耐食性表面被覆鋼板の製造法(遅れ破壊, 圧力容器, 腐食, 腐食割れ, 材料, 日本鉄鋼協会第 112 回(秋季)講演大会)
- 406 落重試験 NDT 温度におよぼす熱影響部の影響(破壊靱性・ステンレス, 性質, 日本鉄鋼協会 第 99 回(春季)講演大会)
- 346 帯状ESW肉盛溶接ビード形状の磁気制御
- 129 鋳ぐるみ法を応用した特殊鋼板の製造 : 鋳ぐるみ法によるクラッド鋼板の製造第 4 報(造塊・連鋳, 製鋼, 日本鉄鋼協会第 94 回(秋季)講演大会)
- アーク溶接過程における水素の挙動(第 3 報) : 被覆アーク溶接金属の拡散性水素源について
- 211 HT50鋼の上向すみ肉溶接部の微視的応力の測定
- 318 上向すみ肉溶接部に発生するトウ・クラックについて
- アーク溶接過程における水素の挙動(第 2 報) : 被覆アーク溶接で母材へ拡散する水素の測定