高窒素 18Cr-10Mn ステンレス鋼の溶接性について
スポンサーリンク
概要
- 論文の詳細を見る
An experimental study was made on the weldability of 18Cr-10Mn stainless steels containing high concentration of nitrogen up to about 0.8%, prepared by a high-pressure melting process in nitrogen atmosphere. Main results obtained are as follows. (1) In the arc welding of high nitrogen 18Cr-10Mn stainless steels, if ordinary welding conditions recommended for welding commercial austenitic stainless steels are adopted, we shall usually be able to get excellent and sound welded joints. (2) In case of welding by using the electrode having the same composition, the tensile strength of welded joints increases in proportion to the nitrogen content of base metals. This strengtheing in the welded joints depends upon the extent of nitrogen diffusion, which occurs from the base metal to the welded metal. (3) The decrease of impact strength in heat-affected zone scarcely occurs even in the steel containing about 0.8% nitrogen. (4) While the base metal is melting, the nitrogen contained in the base metal diffuses and blows out of the metal a little. Consequently, in the base metal containing high concentration of nitrogen i. e. more than 0.65%, blowholes in the weld deposit increase and the concentration of nitrogen in the heat-affected zone decreases a little. (5) But, the decrease of nitrogen content in the base metal occurs only in the limited portion near the weld bond, and the amount of the decrease is small. Therefore, in the steels containing nitrogen less than about 0.65%, the decrease of the nitrogen content scarcely influences the mechanical properties and the microstructures of the welded joints.
- 社団法人溶接学会の論文
- 1972-06-25
著者
関連論文
- 240 蓄勢式摩擦圧接法の圧接機構について (第2報)
- 402 蓄勢式摩擦圧接法の圧接機構について
- 586 Cr-Mo-V 鋼の加速域でのクリープ抵抗に及ぼす微細組織の影響(耐熱鋼, 材料, 日本鉄鋼協会第 104 回(秋季)講演大会)
- 490 Cr-Mo-V 鋼のクリープ損傷(耐熱鋼・耐熱合金, 性質, 日本鉄鋼協会第 102 回(秋季)講演大会)
- 301 快削りん青銅の摩擦圧接
- 314 蓄勢式摩擦圧接法の圧接機構について(第4報) : 摩擦トルクについて
- 444 蓄勢式摩擦圧接法の圧接機構について(第3報) : 寄り速度およびばり形状について
- 高窒素 18Cr-10Mn ステンレス鋼の溶接性について
- 高窒素 18Cr-10Mn ステンレス鋼の点溶接について
- 高窒素 18Cr-7Ni ステンレス鋼の点溶接について
- 597 炭素無添加の 25Cr-35Ni 鋼の第 IV6 及び第 V6 族元素による固溶強化と下部組織との関係(耐熱鋼・耐熱合金, 性質, 日本鉄鋼協会第 102 回(秋季)講演大会)
- PS-23 炭素無添加の 25Cr-35Ni 鋼の第 VIb 族元素による固溶強化と下部組織との関係(性質, 日本鉄鋼協会第 101 回(春季)講演大会)
- 613 Ni-20Cr-4Nb-10W 合金の高温クリープ特性におよぼすβ相の影響(耐熱鋼・耐熱合金, 材料, 日本鉄鋼協会 第 105 回(春季)講演大会)
- 606 Ni-20Cr 合金の高温クリープ特性に及ぼす Nb 添加の影響(耐熱鋼・耐熱合金, 性質, 日本鉄鋼協会第 102 回(秋季)講演大会)