強靭鋼材の熔接割れに就いて第 1 報 : 強靭鋼を熔接する場合起ることある割れの位置及び發生時期
スポンサーリンク
概要
- 論文の詳細を見る
The author has been interested in welding cracks of alloy steels for years and investigated them on all available oceasions. But the questjons of cracking are connected with properties of material, the stress and method of welding, and the scientific illustratoin of cracking remains uncertain. In this report, judging from many facts which the author observed in cases of his inspection of welding factories for alloy steels and confirmed in his laboratory also, he made rough descriptions about welding cracks of alloy steels. Namely, (1) welding cracks were classified with regard to their positions, (2) the relation between the crack in the welding-heat-affected zone, which occurs most frequently among welding cracks, and the maximum hardness of that zone was discussed, (3) and occurrence-time of each welding crack was roughly stated.
- 社団法人溶接学会の論文
- 1948-09-01
著者
関連論文
- 3. 鋼材の熔接性に及ぼす砒素の影響に就て(第 3 報) : 低炭素鋼及び特殊鋼の熔接變質部極大硬度に及ぼす母材含砒量の影響
- 鋼材の熔接性に及ぼす砒素の影響に就て(第 1 報) : 電弧熔着鋼の割れ傾向並に衝撃値に及ぼす熔接棒心線鋼含砒量の影響
- 強靭鋼材の熔接割れに就いて(第 2 報) : 熔接部の横拘束度と熔接縱割れとの關係
- 強靭鋼材の熔接割れに就いて第 1 報 : 強靭鋼を熔接する場合起ることある割れの位置及び發生時期
- 15. 鋼材の熔接性に及ぼす砒素の影響に就て(第 4 報) : 鋼材の鍛接性及ぼす含砒量の影響
- 10. 鋼材の熔接性に及ぼす砒素の影響に就て(第 2 報) : 含砒低炭素鋼心線による電弧熔着鋼の低衝撃値の改良に對する被覆劑中の脱酸劑の効果
- 研究の困難と悦び
- 鋼材熔接部に及ぼす豫熱の影響に就いて
- デューコール鋼材熔接部の變質に及ぼす母材寸法の影響に就いて
- 熔接歪に就いての二三の考察
- 鋼の電弧熔接用電極棒被覆劑の研究(第 5 報) : 市販軟鋼用電極棒の被覆量と熔着鋼の機械的諸性質との關係
- 鋼の電弧熔接用電極棒被覆劑の研究(第 4 報) : Ca(OH)_2-CaF_2-Na_2CO_3 系熔劑に就て
- 鋼の電弧熔接用電極棒被覆劑の研究(第 3 報) : 被覆劑中の黄血鹽の作用
- 鋼の電弧熔接用電極棒被覆劑の研究(第 2 報) : 熔着鋼の見掛の比重及び窒素含量に及ぼす電極棒熔劑の被覆量の影響
- 鋼の電弧熔接用電極棒被覆劑の研究(第 1 報) : 熔着鋼の見掛の比重に及ぼす電極棒被覆熔劑の組成の影響
- 電弧熔着鋼の多孔性に及ぼす諸因子に就て
- 電弧熔着鋼の窒素及び酸素含量に及ぼす諸因子に就て