Cr系不銹鋼板の熔接性 (第4報) : 18Cr鋼板熔接部の脆性に関する一実験

概要

論文の詳細を見る
V-butt multi-layer welding of a 18Cr steel plate, 7.,5mm thick, has been carried out with three kinds of austenite electrodes (A1Sl type 308 316 and 310) and one kind of ferrite-austenite electrodes (all of them,4mm deameter). The obtained welds have been subjected to a hardness test, microstructure test, V-notch Charpy impact test at -200〜+300℃ ; fractographs of the brittle-fractured surfaces in their impact fractures habe been examined and some considerations made on them. Some of the major results are summarized : 1) Transition temperature in the non-affected and the heat-affected zone of parent metal is very high. It is higher in the latter than in the former ; in the latter no annealing effect is observable. 2) Impact value of welds using ferrite-austenite electrodes are in general lower than those of the ones using austenite electrodes. However, excessive lowering of these values does not take place on low temperature side. 3) Fractographs of brittle fractures in the impact fractures of the heat-affected, non-affected zones of parent metal and of welds have been studied to seek the relationship to ductility.
社団法人溶接学会の論文
1957-06-25