It is extremely useful for restoring the decayed tooth if the softened dentin can be rehardened. This study examined the possibility of rehardening the dentin by some ions dissolved from dental cements. The dentin specimens from extracted molars were artificially decalcified and contacted with four types of dental cements. Their changes in hardness, component elements and microscopic structure were pursued by means of Knoop hardness test, X-ray microanalysis and scanning electron microscopy. The effects of the cements on crystallization of calcium phosphate were also investigated for three kinds of synthetic crystal powders by X-ray diffraction. It was found that the glass ionomer cements not only promoted DCPD to transform into hydroxyapatite (HAp) but also increased the crystallinity of poorly crystallized HAp. Although no changes in crystallinity of HAp were obsereved with the zinc-eugenol cements, one of them (Neodyne α) was effective for DCPD to partly transform into HAp. The apatite cement showed no significant effects on the changes of DCPD and HAp. The hardness of the softened dentin showed an increasing tendency when the dentin was contacted with a glass ionomer cement (HY-Bond glas ionomer-C) or an apatite cement (Apatite liner type I). It might be due to the small deposits of calcium salt and increased contents of Ca and P with these cements. A zinc-eugenol cement (Neodyne α) caused a significant increase of hardness in the deeper layer of the dentin. The structural recovery was observed in that layer without any changes in Ca and P contents. In the case of a zinc phosphate cement (Elite cement 100), on the other hand, the hardness of the softened dentin tended to rather decrease. The decalcified dentin might have been further decalcified by the phosphoric acid in the cement. No significant changes in microstructure and Ca and P contents were observed ; however, a small amount of Zn uptake from this cement might have contributed to the long-term recovery of the dentin hardness. From the above results, it is suggested that the dental cements having a possibility of supplying Ca, P or other elements effective for forming HAp and improving its crystallinity may contribute to promote the rehardening of the softened dentin.
- 九州歯科学会の論文
- 1991-02-25
著者
関連論文
- 24. ポーセレン・ラミネートベニア修復の臨床成績 : 短期的観察(第 53 回九州歯科学会総会講演抄録)
- P∿24 ポーセレン・ラミネートベニア修復の臨床成績 : 短期的観察
- 25. 平成 3∿4 年度に第 1 保存部を受診した新患の統計学的調査(第 53 回九州歯科学会総会講演抄録)
- P∿25 平成 2∿3 年度に第 1 保存部を受診した新患の統計学的調査
- 6. リン酸カルシウムの結晶構造に与えるフッ化物添加セメントの影響(第 51 回九州歯科学会総会講演抄録)
- 6∿1030 リン酸カルシウムの結晶構造に与えるフッ化物添加セメントの影響
- 繰り返し加熱処理による耐火模型材の機械的性質ならびに寸法の変化
- 27. 繰返し加熱処理による耐火模型材の圧縮強さと寸法の変化(第 48 回九州歯科学会総会講演抄録)
- P∿27 繰返し熱処理による耐火模型材の圧縮強さと寸法の変化
- インスツルメントの把持に数字表記を用いた教育
- ベース用水硬性リン酸カルシウムセメントの試作
- ポーセレン・ラミネートベニア修復の技工操作とその問題点
- ポーセレン・ラミネートベニア修復の臨床とその問題点
- 8. ハイドロキシアパタイトの X 線回折像による結晶性の観察(第 48 回九州歯科学会総会講演抄録)
- 8∿1040 ハイドロキシアパタイトの X 線回折像による結晶性の観察
- 九州歯科大学附属病院第 1 歯科保存部を受診した初診患者の調査 : 主に再治療の割合について(1991 年度∿1993 年度)
- 耐火性模型材による印象面の再現性
- 試作水硬性リン酸カルシウムセメントの機械的性質
- 1. 水硬性リン酸カルシウムセメントの急性毒性について(第 55 回九州歯科学会総会講演抄録)
- ボンディングシステムの象牙質接着性に及ぼす象牙質前処理剤の効果 -ヒドロキシアパタイトとの接着状態のSEM観察-
- 1∿0930 水硬性リン酸カルシウムセメントの急性毒性について
- 8. ベース材としての水硬性リン酸カルシウム系セメントの開発(第 52 回九州歯科学会総会講演抄録)
- 8∿1054 ベース材としての水硬性リン酸カルシウム系セメントの開発
- 歯科用セメントによる軟化象牙質の硬化に関する研究 : 主論文の要旨
- 歯科用セメントによる軟化象牙質の硬化に関する研究