K-0644 一方向凝固超合金コーティング材の高温低サイクル疲労特性(S06-4 界面強度と高温強度)(S06 コーティング材の力学特性と損傷機構)
スポンサーリンク
概要
- 論文の詳細を見る
The high temperature isothermal low cycle fatigue behavior of an aluminized CoNiCrAlY coated directionally solidified nickel-base superalloy CM247LC with compressive strain holding was studied. Comparison with bare specimens did not show any significant difference in fatigue life. Metallographic observations on bare specimens after testing showed crack initiation from surface oxidized carbides in the interdendritic regions. Coated specimens after testing showed most of the coating cracks stopped in the CoNiCrAlY layer and only part of the cracks extended in the substrate. Oxidation in the coating-substrate interface area seems to play an important role in fatigue property of coated specimens.
- 社団法人日本機械学会の論文
- 2001-08-22
著者
関連論文
- 表面予き裂の疲労き裂伝ぱ挙動に及ぼす引張残留応力場の影響
- 予損傷を受けた結晶制御Ni基超合金中に生成されるセル状変質域の悪影響度低減化の試み : 補修およびリコーティング技術のために
- K-0644 一方向凝固超合金コーティング材の高温低サイクル疲労特性(S06-4 界面強度と高温強度)(S06 コーティング材の力学特性と損傷機構)
- 510 単結晶 Ni 基超合金のリサイクル, リコーティング技術開発への強度的支援
- B-10 高温小型ガスタービンのタービン翼の運転使用による金属組織変化(ガスタービン用先端材料)
- 3903 デジタル画像相関法を用いたき裂開口変位分布計測と疲労き裂伝ぱ速度の評価(S17-1 デジタル画像相関法,S17 実験力学における最近の展開)
- 423 き裂開口変位分布計測に基づく表面疲労き裂伝ぱ挙動の評価 : き裂内部深さに注目して(OS3-5 き裂解析,OS3 エネルギー構造機器の健全性評価と信頼性の高度化3)
- 108 き裂開口変位分布計測と残留応力場の疲労き裂伝ぱ挙動の評価(き裂進展,疲労の機構と強度信頼性,オーガナイスドセッション1,第53期学術講演会)
- 表面き裂の開口変位分布計測に基づく応力拡大係数と疲労き裂伝ぱ速度の評価
- 631 残留応力場の貫通疲労き裂の開口形態と疲労き裂伝ぱ特性(疲労き裂進展)(一般セッション)
- 有限板における貫通き裂の不連続変位分布に基づく応力分布および応力拡大係数の評価法
- 407 表面き裂の開口変位分布計測に基づく応力拡大係数評価と疲労き裂伝ぱ特性
- 発電用ガスタービンの材料技術(ガスタービンの材料技術)
- 1000kW級熱電可変・再生型ガスタービンの開発 (エネルギーソリューション小特集)
- GP1000再生サイクル (特集:高効率ガスタービンの最新動向)
- 三井ガスタービン高温部品の保守技術と寿命評価
- 626 実機使用ガスタービン翼の疲労き裂進展特性評価と回復再熱処理の効果(実機損傷評価,高温環境下における材料の変形・損傷・破壊,オーガナイスドセッション2)