Inclusion Effect on Crack Propagation and Fracture Behavior of P/M Nickel-Base superalloy
スポンサーリンク
概要
- 論文の詳細を見る
Special observations on Al_2O_3 seeded P/M Rene95 superalloy were conducted at SEM in-situ tension loading stage to study the inclusion effect on crack initiation, propagation and fracture behavior of P/M nickel-base superalloy. Experimental results show that, during SEM in-situ tensile process cracks easily initiate at the ceramic inclusions even at very low stress level(lower than yield stress of P/M Rene95). Generally, the cracks nucleate at inclusion/matrix interfaces and easily propagate along the interfaces to the matrix. Sometimes cracks can also directly initiate inside inclusions and propagate in the inclusions till to break the cracked inclusions. Stress concentration field nearby inclusion and the effect of inclusion size and distribution on stress fields were calculated. A proposed model of the inclusion effect on crack and fracture behavior has been discussed in this paper.
- 一般社団法人日本機械学会の論文
- 2001-10-20
著者
-
Zhang Lina
High Temperature Materials Research Laboratories University Of Science &technology Beijing
-
XIE Xishan
High Temperature Materials Research Laboratories University of Science &Technology Beijing
-
DONG Jianxin
High Temperature Materials Research Laboratories University of Science &Technology Beijing
-
LI Xiao
High Temperature Materials Research Laboratories University of Science &Technology Beijing
-
Li Xiao
High Temperature Materials Research Laboratories University Of Science &technology Beijing
-
Xie Xishan
High Temperature Materials Research Laboratories University Of Science &technology Beijing
-
Dong Jianxin
High Temperature Materials Research Laboratories University Of Science &technology Beijing
関連論文
- Inclusion Effect on Crack Propagation and Fracture Behavior of P/M Nickel-Base superalloy
- KL-2-3 The Present Status of Research and Development on Heat Resistant Alloys in China(Keynote Lectures 2)