1015 ロールキャスティングによる積層材の作製(GS-4 材料加工)
スポンサーリンク
概要
- 論文の詳細を見る
Clad strip casting was tried using a single roll caster and two types of twin roll casters. The clad strip could be cast directly from melt. The two pieces of strips could be connected easily by very small force, for example, 5N/mm width. Interface between the strips was formed clearly, and two pieces of strips was connected strongly. To cast strongly connected clad strip, connecting surface had to be semi-solid condition. Both of overlay type clad strip and inlay type clad strip could be cast using the twin roll caster in this study. The clad strip was rapidly solidified like a single strip. Size of copper roll was φ250×100 mm. Roll speed was 20 m/min. Al-12%Si and A1050 were used. Width of the strip was 20〜50 mm. Thickness of the clad strip was 1.5〜3mm.
- 一般社団法人日本機械学会の論文
- 2000-03-16
著者
関連論文
- 336 Al合金の半凝固ロールキャスティングによる機械的性質の向上(OS 加工による材料の機能創製)
- 1507 ロールキャスティング法による複合材料の作製
- 1015 ロールキャスティングによる積層材の作製(GS-4 材料加工)
- 1014 チクソフォーミング用素材の作製(GS-4 材料加工)
- 436 ロールキャスティングによる複合材料の作製(OS 溶融加工)