609 A533B 鋼の高温水環境中の疲労き裂進展挙動と材料異方性の関係
スポンサーリンク
概要
- 論文の詳細を見る
Fatigue crack growth behavior of A533B steel was studied in 288℃ water environment using CT specimens machined from four different orientations of the material with 150mm thick. Fatigue crack growth rate in water at ambient air and in hydrogen gas was also examined. The effects of anisotropy, test frequency, water temperature and hydrogen gas on the crack growth behavior of A533B steel were evaluated. The results show that anisotropy did not have a significant effect on the fatigue crack growth rate in 288℃ water at frequency of 0.5 to 0.05Hz. The fatigue crack growth rate in ambient water was slightly higher than that in 288℃ water and in ambient air. At ΔK above 40 MPa m, the fatigue crack growth rate in hydrogen gas was markedly accelerated compared to that in 288℃ water.
- 2000-10-05
著者
関連論文
- 兵庫県南部地震におけるクレーンの被害調査 (地震に対するクレーンの安全対策に関する特別研究)
- 諸論 (地震に対するクレーンの安全対策に関する特別研究)
- JIS B 8821:2004「クレーン鋼構造部分の計算基準」における疲労設計概要
- 破壊事故からの教訓と指標
- 失敗事例を活用した機械・構造物の損傷防止対策
- F-1407 クレーン構造部分の疲労設計基準の比較(S53-2 限界状態設計法とその適用(2))(S53 限界状態設計法とその適用)
- W07-(1) 技術の変遷と伝承技術 : 災害事例を中心にして(強度研究・技術の伝承に関る問題点と対策)(材料力学部門企画)
- 813 クレーン構造部分の疲労設計基準の見直し
- 609 A533B 鋼の高温水環境中の疲労き裂進展挙動と材料異方性の関係
- 1522 フレッティング疲労強度に及ぼす試験装置およびパッドスパンの影響
- ワイヤロープ用鋼及びSNCM439鋼のフレッティング疲労挙動 (吊上げ用具類の新検査技術に関する研究--クレーン用ワイヤロープの疲労損傷を中心に)
- 産業機械の事故解析事例
- 産業機械の事故解析事例