519 C/Cコンポジットの圧縮挙動に及ぼすマイクロクラックの影響(OS 耐熱材料)
スポンサーリンク
概要
- 論文の詳細を見る
Compressive behavior of 2D and 3D Carbon/Carbon (C/C) composite was investigated. 2DC/C showed relatively linear deformation up to the total fracture. However, 3DC/C showed large nonlinear deformation accompanying the load drop and recovery and no clear fracture was observed. In 2D specimen, the progressive microcracking was not observed during the testing, however, interlaminar delamination was observed. In 3D specimen, the microcracks didn't appear until the first stress peak of the δ-U curve, and after the peak, the delamination between X-Y bundle and shear failure of the Y bundle near the matrix pocket was observed. From the experimental observation, the initiation of the progressive fracture of 3DC/C was supposed as the interlamina delamination, which ruled the fracture of 2DC/C. However, the existence of Z directional fiber prevented the specimen from catastrophic failure. The fracture strength of both the C/Cs was discussed using micro-kinking model by Rosen and shear fracture model by Ewins & Ham.
- 一般社団法人日本機械学会の論文
- 2000-11-24
著者
-
八田 博志
宇宙研
-
後藤 健
宇宙研
-
後藤 健
宇宙航空研究開発機構宇宙科学研究本部
-
仲井 朝美
京工繊大
-
濱田 泰以
京工繊大
-
八田 博志
宇宙科学研究所
-
大谷 章夫
京工繊大
-
デービス イアン
京工繊大
-
大谷 章夫
Jaxa/isas
-
大谷 章夫
岐阜大学 複合材料研究センター
関連論文
- C/C複合材料の高温強度とクリープ挙動
- 2318 C/C複合材料の界面強度測定法(S32-1 セラミックスおよびセラミックス系複合材料(1),S32 セラミックスおよびセラミックス系複合材料)
- 10112 C/C複合材料の耐熱接着技術(製造方法と強度,OS10 先進材料の力学と強度)
- 炭素繊維強化炭素(C/C)複合材料の二軸負荷環境下での破壊挙動
- 3D C/C 複合材料の破壊挙動
- 三次元炭素繊維強化炭素複合材料(3DC/C)複合材料の破壊挙動
- C/C複合材料の繊維強化型SiCコーティングの開発
- 貫通コーティングクラック発生防止を目的としたC/C複合材の耐酸化SiCコーティング
- C/C複合材料上のSiC・C多層耐酸化コーティング
- 平成20年度繊維学会年次大会