206 ダブルメカニカルアロイングしたAl-Ni-Zr非晶質合金粉末の固化成形とその強度特性(OS 粉末加工)

概要

論文の詳細を見る
In order to form high toughness amorphous alloy, double mechanical alloying (DMA) was carried out with Ni-Zr amorphous powder by MA and Al mixed powder, here. Obtained amorphous powders were compacted with vacuum hot press (VHP) method, then the excellent conditions of VHP were found. Also mechanical strength of each compact was measured using 3 point bending tests. As a result, it was understood that Al_<60>Ni_<20>Zr_<14> and Al_<60>Ni_<26>Zr_<14> amorphous powders can be compacted and form compacts which has high strength and toughness, where they were compacted for 1.8ks at 773K with 1000MPa loaded. Furthermore, it was known, as well, that both of deflection and rupture strength decreases as amorphous phases begins crystallization.
一般社団法人日本機械学会の論文
2000-11-24