Reed valves used as part of compressors or engines are frequently subjected to impact fatigue fracture caused by repeated collision against a valve seat or valve stopper, but its mechanism has been made clear yet. In this study the effect of seat shape and valve thickness on the impact fatigue of valve was experimentally investigated with a fatigue machine developed using a fluidic device previously. The results obtained can be summarized as follows. (1) The seat shape which induced complicated motion such as overshoot or torsion in the valve after collision decreased remarkably the impact fatigue life of the valve. (2) Valve thickness did not influence impact fatigue life as evaluated by impact velocity instead of impact force.
- 一般社団法人日本機械学会の論文
- 1994-02-25
著者
関連論文
- 流体素子式疲労試験機の応用 : 90°V曲げ加工した薄板冷間圧延鋼板の両振り平面曲げ疲労強度の評価
- エンジン用バルブ・バルブシ-ト材の高温衝撃摩耗特性
- 有限要素法によるさらばねの解析
- 17-7PH ステンレス鋼の機械的性質に及ぼす熱処理の影響
- 101 焼入れ焼もどし高炭素鋼 (SK5) の疲労強度に及ぼす表面加工の影響
- ばね鋼(SUP10)疲労強度に及ぼす表面仕上げの影響
- 一方向摩擦と往復摩擦における0.42%C炭素鋼の摩耗特性
- 107 ばね鋼 (SUP10) の疲労強度に及ぼす表面処理の影響
- 3-11 13Cr ステンレス鋼の機械的性質に及ぼす焼戻し温度の影響
- 研削条件および後処理が13Cr鋼の疲労強度に及ぼす影響
- 1-3 研削条件およびその後処理が 13Cr 鋼の疲労強度に及ぼす影響
- 平板試験片の縁形状が疲労強度に及ぼす影響
- 研削,ラッピングおよびバレル仕上が 13Cr鋼の疲労強度に及ぼす影響
- 浸炭焼入れ鋼の回転曲げ疲労強度
- 凝着摩耗機構に関する研究--焼なまし炭素鋼同士の乾燥処女面摩擦
- ねじりフレッチング疲労に関する基礎的研究
- 純流体素子式疲労試験機の開発とその応用
- エンジン用バルブ・バルブシート材の高温衝撃摩耗特性 : 第2報,オーステナイト系耐熱鋼SUH36と二つの鉄系焼結材との平面・斜面衝突
- エンジン用バルブ・バルブシート材の高温衝撃摩耗特性 : マルテンサイト系耐熱鋼SUH3と鉄系焼結材との平面衝突の場合
- リード弁の衝撃疲労に関する研究
- 衝撃摩耗に関する基礎的研究 : 大気乾燥下における焼なましS45C炭素鋼の衝撃摩耗特性
- 純流体素子を用いた薄板用曲げ疲労試験機の開発
- 焼なまし炭素鋼の衝撃摩耗特性
- 一方向摩擦と往復摩擦とにおけるアブレシブ摩耗
- 潤滑摩擦下における焼なまし炭素鋼の往復摩耗と一方向摩耗との比較
- 炭素鋼の摩耗と表面層
- 炭素鋼の潤滑摩耗特性と摩耗表面層との関係
- 炭素鋼の摩擦表面に生じた連続硬化層について
- 焼入れ焼きもどし0.42%C炭素鋼の摩耗特性と摩耗表面層との関係
- 炭素鋼の摩擦表面に生じたパッチ状硬化層について
- 焼なまし0.42%Cおよび0.87%C炭素鋼の摩耗特性と摩耗表面層との関係
- 炭素鋼の乾燥摩耗特性におよぼす摩擦相手材かたさの影響
- 軟鋼の摩耗特性と摩耗表面層との関係