IN718の疲労寿命と疲労き裂伝ぱ機構に及ぼす結晶粒径の影響について
スポンサーリンク
概要
- 論文の詳細を見る
Low cycle fatigue tests and fatigue crack growth rate tests were conducted at ambient temperature on fine and coarse-grained IN 718 of which grain size numbers were ASTM No. 10 and ASTM No. 5, respectively. In the low cycle fatigue tests on fine-grained material at maximum stress of 1180 MPa and R=0, fatigue lives of ASTM standard cylindrical specimens ranged from 50000 to 70000 cycles, and every fatigue crack was initiated from the defect on the surface of specimen, i.e., nonmetallic inclusion or carbide. The Fatigue crack growth rate test showed that small surface cracks in the coarse-grained material were propagated considerably faster than those in the fine-grained material. If the small surface cracks started to be propagated from the defects immediately after the start of cyclic loading, the difference in fatigue life between fine-grained material and coarse-grained material resulted from the difference in the small surface crack growth rate.
- 1994-08-25
著者
関連論文
- 高速クラックの動的様相に関する研究 : 第5報 : クラックアレスターの動的解析
- 高速クラックの動的様相に関する研究 : 第4報 : 応力波の影響について
- 高速クラックの動的様相に関する研究 : 第3報 : 造船用鋼材の動的破壊特性
- IN718の疲労寿命と疲労き裂伝ぱ機構に及ぼす結晶粒径の影響について
- 曲げ試験によるPMMAの混合モード破壊挙動
- IN718の極低温破壊機構に及ぼす影響因子
- インコネル718の4Kにおける破壊機構
- 高清浄度ニッケル基超合金の評価技術の進歩(最近のスーパーアロイにおけるプロセス・加工技術の進歩)
- 高速クラックの動的様相に関する研究 : 第4報 : 応力波の影響について
- 高速クラックの動的様相に関する研究(第2報) : PMMAの動的破壊特性