腐食疲れを受けた鋼材のき裂深さと低温ぜい性に関するその後の研究

概要

論文の詳細を見る
In the previous paper, the authors studied on the crack depth of the smooth specimen subjected to corrosion fatigue under cycle frequency of 2 300c/min in saline, and the low temperature embrittlement of the specimens having such corrosion fatigue cracks. In the present paper, the corrosion fatigue is given under cycle frequency of 2 300 c/min in tap water and 760c/min in saline by repeated bending and also under 2 300c/min in saline by repeated twisting to make clear the influence of the crack depth on the embrittlement transition temperature of the materials subjected to corrosion fatigue under more extensive test conditions. The crack depth due to corrosion fatigue depends upon the damage of corrosion fatigue (k-1)/(k_c-1), irrespective of the conditions of corrosion fatigue such as the intensity of corrosive, the nominal stress, the cycle frequency, and either under repeated bending or repeated twisting, where k represents the corrosion effect proposed by the authors and k_c corresponds to k at the rupture time. The crack propagation rate under bending of the nominal stress σ_c is given by a function of the true stress σ_ck acting on the root of the corrosion fatigue crack. The embrittlement transition temperature T_r of the specimens having these cracks rises with the square root of the crack depth and is in a exponential relation to (k-1)/(k_c-1) under wide working conditions of corrosion fatigue.
社団法人日本機械学会の論文
1963-01-25

腐食疲れを受けた鋼材のき裂深さと低温ぜい性に関するその後の研究

スポンサーリンク

概要

著者

関連論文

スポンサーリンク