ローラチェンの疲れ強さについて
スポンサーリンク
概要
- 論文の詳細を見る
Occasionally roller chain fails by fatigue, though abrasion generally seems to be the cause of the failure In this report we considered the life of roller chain from the results of fatigue tests on roller chain. The testing machine used was the Haigh's tension compression fatigue testing machine. The chains applied to the tests was those of the capacity 2,000 kg for a static load. The results obtained were as follows : (1) Fatigue tests were made on chains having the roller links tempered at various temperature, and it was found that the tempering at 450℃ is most suitable for chains used at heavy load. (2) Fatigue tests were made on chains having different forms of roller links, and it was found to be favourable to extend the breadth of the neck of a roller link. (3) Deformation due to fatigue was very small. (4) The value of the notch factor of roller chain is about 3. (5) From the test results the diagrams showing the life of roller chains for fatigue were made.
- 社団法人日本機械学会の論文
- 1951-11-20
著者
関連論文
- 圧入軸の疲れ強さ整理資料
- 鉄鋼材料の疲れにおける寸法効果整理資料
- 鉄鋼材料の切欠き疲れ強さ整理資料
- 鋼の疲れ強さに及ぼす二次応力波の影響
- ローラチェンの疲れ強さについて
- ローラチェインの疲れ強度について
- 鋼および鋳鉄の繰返し引張荷重に対する時間強度について
- 銅および鋳鉄の繰返し引張荷重に対する時間強度について
- 不規則振動疲労研究会報告
- 材料力学研究会
- 石炭酸樹脂の耐摩耗性の研究(第1報)
- 鋳鉄の疲れ強さに及ぼす鋳はだの影響に関する一実験
- 切欠効果に関する研究 : 第4報 帯状突起の影響について
- 切欠効果に関する研究 : 第2報 切欠感度定数について
- 切欠効果に関する研究 : 第1報 Neuberによる形状係数について
- 疲れ強さに関する二三の資料
- 実働荷重と疲れ変化
- 表面圧延による鋼の耐まだら摩耗性改善に関する研究(第2報)
- 二段二重重複繰返し応力の疲れに関する研究-1・2-
- 石炭酸樹脂の耐摩耗性の研究-1・2-
- 切欠効果に関する研究-第1〜4報-
- 経営の体質改善と事務の合理化
- 疲れ破隙の進行について
- 疲れ破隙の進行について
- 表面圧延による疲れ限度向上に関する研究(第2報)
- 表面圧延による疲れ限度向上に関する研究(第1報)
- 表面圧延による疲れ限度向上に関する研究(第2報)
- 表面圧延による疲れ限度向上に関する研究(第1報)
- ころがり接触部の疲れ強さについて
- 石炭酸樹脂の耐摩耗性の研究(第2報)
- 切欠効果に関する研究 : 第3報 切欠角度の切欠係数に及ぼす影響について