チタン酸バリウム磁器の焼結について : 特に高温度における膨脹収縮特性
スポンサーリンク
概要
- 論文の詳細を見る
In order to find out the best firing condition of Barium Titanate ceramics for use as electro-acoustic transducer, we measured at first the thermal expansion and shrinkage characteristics of Barium Titanate at high temperature. Our method of measurement was to observe the variation in length of the test piece continuously as a function of both temperature and time, over the temperature range from room temperature to 1400°C, by means of telescope. The results obtained are summarized as follows.(1) When the temperature was raised from room temperature to 1400°C at the constant rate of 275°C/hr., we found there was an abnormal expansion at 1000°C amounting maximal to 7.5%. This phenomenon seems to be caused by the decomposition of Barium Carbonate.(2) Considering that the sintering phenomenon is the result of the completion of diffusion reaction among particles of solids, we calculated inversely, the reacted quantity of Barium Titanate by the rate of shrinkage and found that Jander's diffusion formula can be applied here. Applying this result, the activation energy of reaction was calculated to be 98kcal/mol.(3) The calculated results with respect to the shrinkage characteristics of Barium Titanate in the firing process nearly coincided with experimental results.(4) By the above mentioned results, we found that when Barium Titanate ceramics are to be fired, sufficient attention must be paid not only for the highest firing temperature and it's duration but also for the raising rate of temperature, especially over the temperature range of abnormal expansion and rapid shrinkage.On applying the obtained results, we made next some further experiments with regard to the difference between the calcined and not calcined material in electrical and acoustic properties of Barium Titanate. We found by the experimental results that the materials which were not calcined had approximately the same quality as those which were calcined, though the former showed slightly higher value than the latter with respect to frequency constant of radial mode vibration.
- 社団法人日本セラミックス協会の論文
- 1957-06-01
著者
関連論文
- 誘電体セラミックス中への不純物の熱拡散
- 11A18 BaTiO_3系磁器の絶縁破壊について
- ホットプレスによるフェライトの製作とその性質
- ホットプレスによるフェライトの焼結過程とその電気的磁気的性質
- ホットプレスしたPbZrO_3の特性 : 誘電体
- ホットプレスによる磁器誘電体材料の焼結過程
- PbOを含む圧電性磁器の焼成過程における異常膨張
- ホットプレスしたチタン酸ビスマスセラミックスの粒子配向と電気的性質
- ホットプレスしたYBa_2Cu_3O_x超伝導セラミックスの特性
- 周辺電極を有する薄円板圧電性磁器振動子の解析
- 微小球状磁器試料の製作
- 空間電荷分極と誘電体吸収現象 : 誘電体
- 3a-D-6 BaTiO_3磁器のAgingと分極反転
- 3a-D-5 BaTiO_3磁器のSpace Charge Polarization
- 無空孔透光性PLZTセラミックスの理論密度とPbO欠陥
- 誘電体粉末の造粒と成形に関する実験的研究
- Microstructure of Ceramic Materials, Proceedings of an American Ceramic Society Symposium, April 27-28, 1963, United States Department of Commerce, 1964, 106頁, 20.5×26.5cm, $1.75.
- 16D-4 チタン酸バリウムの電気傳導
- 高誘電率電磁中の超音波伝播速度と弾性常数の温度依存性
- BaTiO_3磁器の焼成過程と電気的性質
- 9a-F-8 BaTiO_3磁器の生成過程
- (Pb-Sr)(Ti-Zr)O_3系磁器の製造条件と電気的性質
- 粉体の成形に関する実験的研究, 特に円筒形磁器圧電振動子の製法
- ホットプレスした透光性圧電セラミックスの電気的,光学的性質(第1報)
- 超伝導YBa2Cu3Oxセラミクスの諸特性と空孔構造
- PbTiO3-(Bi1/2Na1/2)TiO3系セラミクスの焼結と圧電的性質
- フェライト多結晶体における非直線電気伝導
- NiZnフェライトの微細構造と磁気的性質
- チタン酸バリウム磁器の焼結, 特に高温度におけるCO_2の放出過程について
- フラックス法で合成した粉末を用いたPLZTセラミクスの電気的,光学的性質
- チタン酸バリウム磁器の焼結について : 特に高温度における膨脹収縮特性