BaTiO_3磁器の焼成過程と電気的性質

概要

論文の詳細を見る
The continuous-dilatometric method for the measurement of the change of dimension during the firing of the equimolecular mixture of BaCO_3 and TiO_2,the X-ray diffraction for following after the reaction and the formation of BaTiO_3,and the electron microscope for the observation of the progress of grain growth, were used for the investigation of the relation between the growth of microcrystals and some electric properties, especially the D.C. break down voltage and hysteresis curves with results as follows : ( I ) BaTiO_3 was formed from about 700℃ and finished at the temperature of maximum expansion (at about 1100℃), which suggest the existence of a close relation between the anomalous expansion and the formation of BaTiO_3. ( 2 ) The microcrystals began to grow from about 1250℃, which was accompanied by the rapid increase of relative permittivity. The Curie point, however, remained unaffected by the change of firing temperature from 1200゜〜1400℃. ( 3 ) The trend of rather decreasing break down voltage by the overgrowth of the microcrystals was observed. The relation between the break down voltage and the thickness of the specimen and the holding time at the maximum firing temperature (1360℃) was found to be expressed by ; 2hrs holding V_c 2hr=9xd^<0.726> (kV) 16hrs holding V_c 16hr=6.7xd^<0.788> (kV), where V_c is the break down voltage, and d the thickuess in mm. ( 4 ) Hysteresis curves showed that space charge polarization is more liable to occur by the incomplete growth of microcrystals. [Received February 12,1962]
社団法人日本セラミックス協会の論文
1962-09-01

BaTiO_3磁器の焼成過程と電気的性質

スポンサーリンク

概要

著者

関連論文

スポンサーリンク