As_2S_3-Tl_2S系およびAs_2S_3-Ag_2S系のガラスの構造
スポンサーリンク
概要
- 論文の詳細を見る
Glass-forming region in the system As-S-Tl has been re-examined because the procedure of Flaschen et al. is doubtful on the point of homogeneous melting free from oxygen contamination. The As-S-Tl glass-forming system was found to be substantially comparable with the As-S-Ag glass-forming system reported already (Fig. 1).Such properties as density, thermal expansion and infrared absorption have been measured on As2S3-Tl2S and As2S3-Ag2S glasses (Figs. 2 to 6). Both glasses exhibited some new absorption peaks in their infrared spectra in addition to the peak at 698cm-1 observed for As2S3 glass and these peaks were most distinct at the composition TlAsS2 or AgAsS2. On the basis of the crystal structure of As2S3 (orpiment), TlAsS2 (rolandite), AgAsS2 (trechmannite or smithite) and Ag3AsS3 (xanthoconite or proustite), the assignment of the peaks observed for As2S3, TlAsS2 and AgAsS2 glasses was made using the equation v=A(r-B)-3/2, where v, r, A and B are wave number, bond length and constants, respectively (Fig. 7). All the peaks observed may be assigned to the vibration of As-S bond with different bond length and, on the other hand, the absorption peaks calculated for the compounds As2S3, TlAsS2 and AgAsS2 agreed very closely with those observed experimentally for the corresponding glasses (Fig. 8). Consequently the above each glass may be considered to have the structure similar to that of the corresponding compound. Furthermore, it may be assumed that the absorption peak would be observed nearly at 696cm-1 if a glass could be obtained at the Ag3AsS3 composition (Table 1).In view of the above facts the most reasonable conclusions to be drawn from the infrared absorption and density data are the followings: The structure of skeleton composed of As and S changes successively as Tl2S or Ag2S is added to the As2S3 glass. In the case of the As2S3-Tl2S glasses orpiment-like (AsS3/2)n sheet structure transforms to (AsS2)n chain structure found in rolandite and then to short chain structure. On the other hand, in the case of the As2S3-Ag2S glasses (AsS3/2)n sheet structure transforms to discrete As3S6 group structure found in smithite or trechmannite and then to isolated AsS3 pyramid structure found in xanthoconite or proustite.
- 社団法人日本セラミックス協会の論文
- 1974-09-01
著者
関連論文
- MF_n-BaF_2-YF_3-ErF_3(M:Zr,Hf.Al,Ga,In,ScあるいはZn)系ガラスにおけるEr^アップコンバージョン蛍光
- 重クラウン系光学ガラス研磨面の表面化学的研究
- 赤外線吸収スペクトルによる硼珪酸塩ガラス中の硼素配位数に関する研究
- グラスライニング座談会
- ハロゲン化物ガラスにおける希土類イオンの光遷移特性と波長変換素子
- フリント系光学ガラス研磨面の表面化学的研究
- As-S 系ガラスの赤外線吸収スペクトルについて : 硫化物ガラスの物性と構造 I
- As-S 系ガラスの構造に関する研究 : 赤外線吸収スペクトルよりの推論
- 重クラウンガラスのアルカリ溶液による侵蝕
- A8.ガラスに対するアルカリ侵蝕に及ぼすカチオンの影響(研究発表講演要旨)
- A5.ガラスのアルカリ侵蝕におけるカチオンの影響(研究発表講演要旨)
- 重クラウン系光学ガラスの有機酸による侵食
- Na_2O-CaO-SiO_2ガラスのアルカリ溶液による侵食
- 神戸大学理学部創設期の化学科について (神戸大学開学前後の各部局について)
- As_2S_3-Tl_2S系およびAs_2S_3-Ag_2S系のガラスの構造
- K_2O-BaO-V_2O_5,K_2O-ZnO-V_2O_5およびBaO-ZnO-V_2O_5系ガラスの物性
- 光学ガラス表面の酸によるくもり
- As_2S_3-Sb_2S_3-S系ガラスの物性と構造 : 硫化物ガラスの物性と構造V
- As-S系ガラスの熱膨張
- As_2S_3-Sb_2S_3系ガラスの物性と構造 : 硫化物ガラスの物性と構造, IV
- As-S系ガラスの構造について : 硫化物ガラスの物性と構造, III
- As-S 系ガラスの物性(硫化物ガラスの物性と構造 II)
- 光学ガラス研磨面の小量溶液による侵蝕
- Surface Properties of Silicate Glass
- 海外通信
- アメリカ便り : Stanford Research Instituteにて
- ガラス表面における水蒸気の凝縮
- 2 窯業における応用
- ガラスの表面化学