CF/Epoxy複合材料の機械的特性に及ぼすポストキュアの効果(<特集>複合材料)
スポンサーリンク
概要
- 論文の詳細を見る
This paper presents the effect of post-cure on mechanical properties of CF/Epoxy composites. At first, the shrinkage strain and the mechanical properties such as Vickers hardness of resin, transverse modulus and strength are measured for carbon/epoxy unidirectional laminates after four-hour thermal treatment (post-cure process) at temperatures ranging from 70℃ to 200℃. Then, the effect of post-cure temperature on transverse cracking behavior in a cross-ply laminate is experimentally investigated. The change in the residual stress due to post-cure is also estimated for the cross-ply laminate. Finally, the fracture surfaces of transverse cracks are observed using the scanning electron microcopy (SEM) to reveal the effect of post-cure on fracture behavior. It is found that the unidirectional laminate shrinks in only the transverse direction after the post-cure process. The hardness of the resin increases with increasing post-cure temperature below 150℃ while transverse modulus and strength are independent of post-cure temperature below 150℃. Transverse cracking in post-cured cross-ply specimens initiates at lower stresses than the critical stresses in virgin specimens. The transverse crack density is predicted by a Weibull's probabilistic failure model. It is deduced from SEM observation of fracture surfaces that the fiber/resin interface is weakened by thermal treatment that may lead to reduction in the transverse strength at 200℃.
- 社団法人日本材料学会の論文
- 2002-05-15
著者
関連論文
- 圧縮負荷下における肝臓の機械的性質
- 第14回国際複合材料会議報告
- ランダム配向不連続炭素繊維強化ガラス基複合材料の破壊メカニズム
- CFRP一方向材の非線形変形挙動に及ぼすひずみ速度効果
- ポリカーボネートの二段二重変動荷重下の疲労寿命
- ポリカーボネートの疲労き裂発生と破断寿命に及ぼす環境効果
- CFRP一方向板のインピーダンスモデル
- 柔軟樹脂で繊維端を被覆した短繊維強化複合材料の弾性シアラグ解析
- 希薄なガラス繊維強化フェノール樹脂の疲労破壊挙動に及ぼすカップリング剤の効果
- ポリサルホンの疲労き裂進展挙動
- 高分子材料の疲労特性に及ぼす環境効果
- CF/Epoxyの非線形引張応力-ひずみ挙動に及ぼす温度の影響(高分子系複合材料)
- GFRP一方向板の電気抵抗に及ぼす負荷履歴の効果
- 炭素繊維強化プラスチックの電気的特性とその応用
- CF/Epoxy複合材料の機械的特性に及ぼすポストキュアの効果(複合材料)
- サリー大学滞在記