硬質塩化ビニルの耐薬品性評価法
スポンサーリンク
概要
- 論文の詳細を見る
The chemical resistance of unplasticized polyvinyl chloride (HPVC) was investigated in several organic solvents at room temperature by using the static and dynamic test methods, and the results ere compared with the data in service. The results showed that the estimation of the chemical resistance of HPVC was rather difficult by the measurements of weight, hardness and tensile properties even after testing for 7〜30 days. On the other hand, the creep and stress relaxation test results gave good agreement with the data service. From these results, a way for evaluating chemical resistance of HPVC by the stress relaxation test method was established, which gives the result in a relatively short time.
- 社団法人日本材料学会の論文
- 1979-09-15
著者
関連論文
- 硬質塩化ビニルの耐薬品性評価法
- アンモニア貯蔵タンクの腐食割れの挙動と原因について
- Y-TZPの機械的性質及び微細組織に及ぼすAl_2O_3添加の影響
- 正方晶ジルコニアの破壊挙動について
- 298 オーステナイト系ステンレス鋼管矯正条件の残留応力および耐応力腐食割れ性におよぼす影響(ステンレス鋼の耐食性, 性質, 日本鉄鋼協会 第 97 回(春季)講演大会)
- 化学プラントにおける炭素鋼の環境脆化と対策
- W24-(3) FRP 材の劣化診断事例紹介 : 酸・アルカリによる FRP の劣化現象とその検査
- プラント材料の腐食劣化と診断技術(腐食防食小特集)
- 金属材料の環境劣化における非破壊検査と寿命予測 (化学プラントにおける材料の損傷と寿命予測)
- ステンレス鋼製熱交換器チュ-ブの応力腐食割れ防止法
- ステンレス鋼チュ-ブの応力腐食割れに及ばす残留応力の影響
- 低合金鋼構造物の環境脆性割れとその対策(化学装置の使用中損傷とその防止対策)
- 熱交換器の余寿命予測の現状に関する調査 : ワーキンググループ「熱交換器余寿命予測」の活動報告(腐食防食)
- タンタルの水素ぜい化の評価法(腐食防食)
- カーボンセメントの表面観察による腐食評価法(腐食防食小特集)
- 電気化学的再活性化法による硫安液の粒界腐食作用の評価(腐食防食小特集号)
- 樹脂ライニングの劣化評価法の基礎的検討 : (腐食防食小特集)
- 極値解析の実プラント腐食問題への適用におけるパラメーター推定法による差異(腐食防食)
- 腐食の事例と対策 : 8.腐食の診断技術と寿命予測(建設材料特集)
- 化学装置用材料とその進歩