タンタルの水素ぜい化の評価法(<特集>腐食防食)
スポンサーリンク
概要
- 論文の詳細を見る
Tantalum is used in a chemical plant as an excellent corrosion resistant material. But occasionally it suddenly causes embrittlement fracture by absorbed hydrogen. In this study, the effect of hydrogen absorption on its electrical properties has been studied. Tantalum showed the embrittlement at 250 ppm of hydrogen, which appeared as the decrease of elongation and reduction of area in the tensile test. On the other hand, the eddy current test showed a distinct dependence on absorbed hydrogen even at 150 ppm, which scarcely appeared on the mechanical properties and electric resistivity. Therefore, the eddy current test is a more sensitive method for the evaluaion of hydrogen embrittlement of tantalum.
- 社団法人日本材料学会の論文
- 1995-11-15
著者
関連論文
- 硬質塩化ビニルの耐薬品性評価法
- 298 オーステナイト系ステンレス鋼管矯正条件の残留応力および耐応力腐食割れ性におよぼす影響(ステンレス鋼の耐食性, 性質, 日本鉄鋼協会 第 97 回(春季)講演大会)
- 化学プラントにおける炭素鋼の環境脆化と対策
- 亜鉛溶射による液体アンモニアタンクの腐食割れ防止
- W24-(3) FRP 材の劣化診断事例紹介 : 酸・アルカリによる FRP の劣化現象とその検査
- プラント材料の腐食劣化と診断技術(腐食防食小特集)
- ステンレス鋼チュ-ブの応力腐食割れに及ばす残留応力の影響
- 低合金鋼構造物の環境脆性割れとその対策(化学装置の使用中損傷とその防止対策)
- 熱交換器の余寿命予測の現状に関する調査 : ワーキンググループ「熱交換器余寿命予測」の活動報告(腐食防食)
- 化学装置用材料の信頼性について(腐食防食)
- タンタルの水素ぜい化の評価法(腐食防食)
- カーボンセメントの表面観察による腐食評価法(腐食防食小特集)
- 電気化学的再活性化法による硫安液の粒界腐食作用の評価(腐食防食小特集号)
- 樹脂ライニングの劣化評価法の基礎的検討 : (腐食防食小特集)
- 極値統計法による化学プラントの腐食評価法に関する研究
- 極値解析の実プラント腐食問題への適用におけるパラメーター推定法による差異(腐食防食)
- プラント腐食への極値解析の応用
- 検査手法の実際 (伝熱と熱交換器) -- (熱交換の保守管理)
- 腐食の事例と対策 : 8.腐食の診断技術と寿命予測(建設材料特集)
- 化学装置用材料とその進歩