炭素鋼の疲労強度に及ぼすねじり塑性加工の影響
スポンサーリンク
概要
- 論文の詳細を見る
Hereunder is presented a report of studies made on the influence of preliminary workings on the fatigue strength of carbon steel. The effects of residual stress and structural change that are produced by cold-workings on the fatigue strength are discussed. For the increase of fatigue strength, in the case of uniaxial deformation like tension or compression, as previously reported, the structural change is considered to be more responsible than residual stress. In the case of biaxial deformation like torsion, however, these fatigue behaviours are not clarified yet. In this paper, the effect of torsional preliminary working on the fatigue strength of S45C steel is discussed in comparison with that of tensile and compressive preliminary workings. The results obtained are summarized as follows : (1) The residual stress produced by torsional deformation assumes a shearing state in the direction counter to the twisting direction that has been previously given. (2) The materials subjected to preliminary workings, in plastic deformation by three kinds of strain, twisting, stretching and compressing, each to equal level of degrees, have shown increase in fatigue strength quantitatively in the descending order as follows ; twisting strain > stretching strain > compressing strain (3) The fatigue limit of twisted specimen continues to increase until such a straining as ε*=0. 400, and then it tends steeply to decrease. Considering the stress strate of twisted specimens, it is concluded that the residual stress due to the preliminary working does not affect the fatigue limit, although the apparent stress amplitude increases with the shearing residual stress. The fractured surface is considered as apt to be preliminary influenced by the shearing residual stress. (4) From the results of the tension test and the compression test of each strained specimen, it is apparent that the yield point for reversal direction of the deformed direction is lower than that of the annealed specimen because of Bauschinger's effect in the case of stretched and compressed specimen. On the other hand, the yield points in both the tensile and the compressive directions in the case of twisted specimen increase over that of the annealed specimen. These anisotropy of work-hardening is considered to contribute to the result that the fatigue strength of twisted specimen is largest among the preliminary strained specimens in the same amount of equivalent plastic strain by the three kinds of straining processes.
- 1971-12-15
著者
関連論文
- 炭素鋼の疲労強度に及ぼすねじり塑性加工の影響
- 負荷応力とき裂伝ぱ速度との関係に及ぼすマトリックス結晶組織の影響
- 疲労き裂先端の応力状態の細束X線による検討
- 純アルミニウム粗大結晶試料における疲労損傷について
- 高周波焼入材の疲労強度に及ぼす焼もどし温度の影響について
- (1-17) 疲労き裂先端の応力状態の細束 X 線による検討
- (1-11) 純アルミニウム粗大結晶における疲労損傷について
- 炭素鋼の疲労強度に及ぼす予加工の影響に関する研究
- 細束X線回折法による疲労の研究
- 1-26 塑性変形によって生ずる相応力と疲労強度について
- 1-1 低炭素鋼の疲労過程中における試験温度の結晶組織変化に及ぼす影響
- 疲労中の試験温度の結晶組織変化に及ぼす影響
- 高周波焼入材の疲労強度向上に及ぼす要因について
- 炭素鋼の疲労強度に及ぼす引張りおよび圧縮塑性加工の影響
- 高周波焼入材の疲労強度に及ぼす硬化深さ,および残留応力の影響
- 平均応力の疲労き裂伝ぱ速度への影響と細束X線によるき裂先端の結晶組織の観察
- X線による切欠き材の疲れ破壊に関する研究 : 細束X線技術による焼なまし低炭素鋼における疲れき裂先端近傍の結晶変形の観察
- X線による切欠き材の疲労破壊に関する研究 : 細束X線による冷間圧延加工した低炭素鋼材における疲労の観察II
- X線による切欠き材の疲労破壊に関する研究(細束X線による冷間圧延加工した低炭素鋼材における疲労の観察 I)
- X線技術による切欠き材の疲れ破壊に関する研究 : 細束X線技術による焼なまし低炭素鋼における疲れき裂先端近傍の結晶変形の観察
- X線による切欠き材の疲れ破壊に関する研究 : 細束X線による焼なまし鋼材における疲れの観察
- X線による切欠き材の疲れ破壊に関する研究 : 細束X線による焼なまし鋼材における疲れの観察
- X線による切欠材の疲労破壊に関する研究 : 切欠底における残留応力変化について
- X線による切欠材の疲労破壊に関する研究 : 切欠底における組織変化とX線回折線半価幅の変化について : X線応力測定特集号
- X線による切欠き材の疲労破壊に関する研究 細束X線による焼入時効した低炭素鋼材の疲労の観察 (X線材料強度特集号)