平均応力が変動する条件下における等価両振り応力に関する一考察

概要

論文の詳細を見る
The fatigue test of 7075 T 6 aluminum alloy under constant mean stress σ_m in the range of 0.20≦A≦∞ (A=σ_a/σ_m) was carried out by use of a testing machine of Schenck type. Also, the fatigue test under cyclic varying mean stress σ_m' was performed by a newly constructed cyclic creep testing machine. From these tests, the following results were obtained: (1) From the results of fatigue test under constant mean stress, the equivalent alternating stress σ_<ae> was determined. The curve for the relation between σ_<ae>/σ_a and A was found to be represented nearly by two linear lines with a junction point at A=0.5〜0.7. It was also found that the fatigue life curve in the range of A>0.5〜0.7 was nearly parallel to that under fully reversed stressing (A=∞) but in the range of A<0.5〜0.7 it was not parallel. (2) From the results of fatigue test under cyclic varying mean stress with secondary stress superimposed, the equivalent alternating stress σ_<ae> was also determined and the curve for the relation between σ_<ae>/σ_a and the stress ratio of σ_a to σ_m, A', was represented by two curved lines with a junction point at A'=0.5〜0.6. In the range of A'<0.5〜0.6 the curve was nearly a straight line, in the range of 0.5〜0.6<A'<0.8 it showed a convex toward the upper direction and in the range of A'>0.8 it was again nearly a straight line. (3) From the results of fatigue test under cyclic varying mean stress without secondary stress, the equivalent alternating mean stress Y_e and the varying mean stress, Y=1/(√<2>) (σ_m'-σ_m), were determined. It was found that the relation between Y_e/Y and the stress ratio A' (=Y/X) was represented by a similar curve given in (1) and (2).
社団法人日本材料学会の論文
1976-06-15

平均応力が変動する条件下における等価両振り応力に関する一考察

スポンサーリンク

概要

著者

関連論文

スポンサーリンク