The fatigue phenomena due to pulsating repeated bending in a large plate specimen of spring steel which had been surface-strengthened by shot-peening were investigated experimentally. The change in the surface residual stress during fatigue process and the roughness in the fractured surface after rupture were measured by X-ray and surface roughness tester and the fractured surface conditions were observed under the optical and electron microscopes. The results obtained are as follows. (1) Up to the time just before a rupture in the fatigue process, the surface residual stress on the tension side changes only slightly, but just before the rupture it drops sharply. On the compression side, regardless of the measured position, the stress diminishes remarkably in the initial stage of the fatigue process, followed by a slight decrease continuing up to the occurrence of a rupture and then by a sharp drop just before the rupture. (2) A Iarge number of fatigue cracks initiate near the boundary between the surface-strengthened layer on the tension side and the non-strengthened inside. These cracks propagate at a velocity of about O.5〜4.O×1O_<-4>mm/cycle and, coupled with an acceleration of failure, Iead to a rupture. Thus, the fractured surface presents a complicated look with coexistence of a fatigue fracture and a fracture by accelerated failure. (3) The electron microscope observation showed coexistence of complicated striation patterns and dimple patterns at the fatigue fracture surface.
- 社団法人日本材料学会の論文
- 1972-12-15
著者
関連論文
- ショットピーニング加工を施した大型ばね鋼板の疲労現象について
- 止端の疲れ破壊における溶接線の傾きの影響
- 硬質塩化ビニル管材に加工を与えた際に生ずる二,三の現象
- (34) 止端の疲れ破壊における溶接線の傾きの影響(昭和 41 年度春季全国大会講演概要)
- 表面ロール加工を施した黄銅およびジュラルミンの疲れ限度
- 表面ロール加工をほどこした黄銅およびジュラルミンの疲れ強さ
- 位置敏感形検出器による疲労被害の検出 : 回折X線プロファイル変化の特性(X線材料強度小特集)
- 多結晶金属材料におけるX線回折現象