FRPの機械的性質 : 積層GRP板の各層における基材の影響
スポンサーリンク
概要
- 論文の詳細を見る
Glass fiber reinforced polyester laminates (GRP) have recently found a wide industrial application and the mechanical properties of the laminates have often been reported. However, few are really studied based on a well-organized experimental method. The purpose of our investigations is to study the following effects using the orthogonal array table type L_<81>. (1)The effects of the kinds of base materials in each layers on mechanical properties of GRP. (2)The effects of the molding conditions on mechanical properties of GRP. The test samples were prepared by the hand lay-up molding method with three kinds of base materials which are shown in Table I and Fig.3. Using the test pieces from the samples, tensile strength, tensile modulus, flexural strength, flexural modulus and thickness were measured in the atmosphere of 20±℃, 65±2% R. H. and the following results were obtained. (1)The force applied to a tensile test piece seems to be uniformly distributed into each layer of the laminates. (2)When the laminates is used as a bent member, the effects of the kinds of base materials are scarcely influenced by the adjacent base materials, and the farther the base material is located from the central layer, the larger become the effects. In ten plies of laminate, The effects of the kinds of the interior four base materials can be neglected. (3)It is advisable not to use woven roving on compression side of bent members. (4)The slower the rate of resin curring is, the stronger products can be obtained. (5)Differences breaking stresses and moduli are not noticeable between the samples molded by the man of experience and one of inexperience. (6)The screw roller brought a good result in lamination of satin-like weavings, and mohair and wool rollers brought good results in lamination and resin impregnation of the woven rovings. The washer roller gave only bad result for all base materials. (7)After-curring of the sample caused lower tensile strength and modulus with higher flexural strength and modulus. After-curring of the test pieces subsequent to machining caused higher strength and modulus than curring prior to machining. (8)Wider specimens improve apparent breaking stress and modulus.
- 社団法人日本材料学会の論文
- 1972-10-15
著者
関連論文
- CFRP積層板の落錘衝撃損傷と衝撃吸収エネルギーの関係に及ぼす積層構成の影響(衝撃)
- 擬似等方性カーボン/エポキシ積層板の落錘衝撃損傷進展
- 平織カーボン/エポキシ積層板の落錘衝撃損傷
- 電解を応用した加工と処理
- 硬質プラスチックの疲労強度に及ぼす試験条件の影響
- 335 熱可塑性プラスチック保存試料の衝撃値の経年変化(続報)
- 306 高分子材料の微小せん断特性に及ぼすダイスの締付圧の影響(高分子材料)
- 313 ガラス繊維強化ポリプロピレンに対する微小せん断試験法の適用(高分子,複合材料)
- 312 プラスチックの見かけ曲げ弾性率の補正法(高分子材料)
- フェノール樹脂積層板の回転曲げ疲労試験
- 電解研磨に関する研究-4-
- 電解研磨に関する研究-3-
- 樽式電解研磨法の研究
- 電解研磨の限界流電に関する研究
- CFRPの曲げクリ-プ試験における負荷速度について
- 科研式迅速摩耗試験機を利用したプラスチックの摩耗試験方法
- 試験片打抜刃がプラスチックスの引張特性に及ぼす影響について
- "複合材料術語辞典" 複合材料術語辞典編集委員会(編) 1994年, アグネ承風社, B6判, 395ページ, 定価3605円
- 313 プラスチックの曲げクリープ試験における負荷速度の影響(高分子材料II)
- 332 プラスチックのクリープ伸び測定法に関する研究 : 第 1 報伸び計の取りつけ方法について
- 3-7 プラスチックのクリープ試験法に関する研究 : 相似試験片におけるクリープ破断強さの測定
- FRPの機械的性質 : 積層GRP板の各層における基材の影響
- 3-7 補強材の積層枚数を変えた FRP の機械的性質
- FRPの機械的性質 : 直交配列に基づく諸因子の影響
- 熱可塑性樹脂の疲労試験
- プレストレストコンクリートの新しい方法による製造実験に関する研究
- プラスチック板の曲げ弾性係数について
- プラスチック板の縦弾性係数を簡易に推定する方法
- プラスチックの線形粘弾性に対するスペクトル表示法に関する一提案
- フェノール樹脂積層板の成形圧力と回転曲げ疲労強度等の二,三の機械的性質との関係について
- スタンダーダイジングボックスの改良
- スタンダーダイジングボックスの改良
- 電解研磨による微少形状の変化