SCM3の水素ぜい化と遅れ破壊 (<小特集>X線材料強度小特集)
スポンサーリンク
概要
- 論文の詳細を見る
Static tensile tests and cantilever bending delayed fracture tests were performed on Cr-Mo structural steel V notched specimens which had been dipped into 5 % H_2SO_4 solution to introduce hydrogen beforehand and tempered at the range from 250℃ to 600℃. The results obtained are as follows. (1) The materials tempered at lower temperatures or having higher strength levels show a noticeable decrease in notch strength by hydrogen charge. (2) There is a good correlation between the delayed fracture limit and the notch strength after hydrogen charge. (3) The delayed fracture sensitivity varies remarkably with tempering temperature from 350℃ to 500℃, corresponding to 120〜160 kg/mm^2 in tensile strength, 320〜480 in Vicker's hardness, and 2.6〜4.2 degree in half value breadth. (4) Hydrogen sensitivity is affected by the residual stress near the surface caused by heat treatment and it increases with tensile residual stress. (5) The microfracture mode changes depending upon the magnitude of delayed fracture sensitivity.
- 社団法人日本材料学会の論文
- 1978-03-15
著者
関連論文
- 遅れ破壊強度に及ぼす表面処理残留応力の影響について
- Ni-Ti合金の形状記憶特性について
- 衝撃強さとAE発生の相関について(第2報)
- 衝撃強さとAE発生との相関について
- アモルファス合金の熱的安定性と水素ぜい化について
- エックス線による多結晶金属材料の変形に関する研究
- 高強度鋼の水素誘起現象に及ぼす水素侵入方向の影響について
- 800MPa級炭素鋼の水素ぜい化に及ぼす炭素含有量の影響
- 高強度鋼の水素ぜい化に及ぼす水素浸入深さの影響について
- 遅れ破壊強度に及ぼす表面処理硬度の影響について
- 129 高強度鋼の水素ぜい化に及ぼす水素吸蔵方向の影響について(溶融金属ぜい化・水素ぜい化割れ)
- 耐熱金属材料のX線応力測定に関する研究 : ニッケル基合金材の高温弾性定数, 残留応力について(X線材料強度小特集)
- 213 遅れ破壊強さに及ぼす表面処理硬度の影響(遅れ破壊,破壊靱性)
- X線による耐熱金属材料の弾性定数測定
- 234 耐熱金属材料の X 線応力測定 : ニッケル基合金の高温における残留応力と組織
- 206 遅れ破壊強度に及ぼす表面処理効果について
- 耐熱金属材料の高温におけるX線応力測定
- 耐熱金属材料のX線応力測定に関する研究 : ニッケル基合金材のX線的弾性定数について(X線材料強度小特集)
- SCM3の水素ぜい化と遅れ破壊 (X線材料強度小特集)
- 耐熱材料のX線応力測定法に関する研究--ニッケル基合金のX線的弾性定数について
- 高張力の遅れ破壊に関する基礎的研究
- Al-Zn-Mg系合金のX線応力測定に関する研究
- 3-24 高張力鋼の水素ぜい化と遅れ破壊について
- ぜい性塗膜法およびX線法による測定応力の相関--塗膜の増感について
- SCM2の遅れ破壊について
- 高張力鋼の遅れ破壊について
- 高張力鋼の水素ぜい化について
- 多結晶金属の高温負荷時のX線測定について
- X線法およびぜい性塗膜法による測定応力の相関