Uと2SALとの関連変形について
スポンサーリンク
概要
- 論文の詳細を見る
The authors have investigated two fundamental experiments on the deformation behaviours of the aluminium sheath which might be restricted by the uranium fuel core, for exsample, as the combination of the uranium rod and the aluminium sheath used for the fuel element of JRR-3 type reactor. The first experiment was studied for the stress behaviour and the micro structure changes etc. of extruded 2S aluminium which was subjected to the same length changes as that of β-quenched uranium under the thermal cycling between 110^○ and 550℃. In this case, the experiment was done under the condition separated the uranium rod and the aluminium sheath from each other. The second one was studied to clarify the systematic deformation behaviour of the aluminium caused by the thermal growth of the uramium for reference to the first results, and then the experiments carried out for the repeated strain cyclic tests with the growth of constant rate of five kinds in the tensile direction only, that is , 0, 0.020, 0.037, 0.053 and 0.074 per cent per cycle, respectively. In these experiments, the strain cyclic amplitude, the test temperature of 2S aluminium and time per cycle was about 0.59 per cent strain, 75℃ and 27.5 min., respectively. The testing machine used was "the universal thermal fatigue testing machine" which was designed by the authors. The outline of the experimental results was as follows : The effect of the growth was clarified to accelerate the local deformation of 2S aluminium from these results, and consequently the fatigue life decreases with increase of the growth rate per cycle, and the relation between the growth rate per cycle and the logarithm of cycles to failure was approximately presented by a straight line. The degree of softening and gardening to be caused by strain cycles with the growth and the time for softening and hardening depended upon large or small of the growth rate per cycle. Furthermore, it was defined from the point of view of the microstructure behaviour that the changes of microstructure due to progress of the deformation follow the same process in spite of large or small of the growth rate per cycle, but the progress rate of the microstructure change becomes late with decrease of the growth rate per cycle. That is, it dependens apparently upon the number of various deformation bands and their forms. The experiments showed that the growth and the strain cycle have the reversal effect on the changes in strength each other, and this opposite phenomenon was explained from the point of view of the microstructure changes between the repeated strain cycle and the simple tension.
- 社団法人日本材料学会の論文
- 1963-03-15
著者
関連論文
- かたさ測定による金属の低温ぜい化の検出(ビッカースかたさと引張性質の温度依存性の相関性について)
- かたさによるモリブデンとタングステンの低温ぜい化に関する研究
- ベリリウム押出し材の高温強度に関する研究(高温強度小特集)
- ベリリウム圧延材の高温強度に関する研究(高温強度小特集)
- 熱サイクル後の炭素鋼の強度および疲労に及ぼす非金属介在物の影響について
- ビッカース圧痕周囲の変形とかたさの温度依存性との関係について
- 原子炉構造用鉄鋼材料の照射脆化の研究
- 3-9 原子炉用黒鉛のヤング率に及ぼす圧縮応力の影響
- ウラニウムとMagnox A-12との関連変形
- Uと2SALとの関連変形について
- 熱サイクルによる原子炉用金属材料の変形について : 高温強度特集号
- 140 原子炉構造用鉄鋼材料の照射脆化の研究(工具鋼・低温用鋼およびその他, 日本鉄鋼協会第 68 回(秋季)講演大会講演論文集 (II))
- 冷間加工後の特殊鋼線に及ぼす低温燒鈍の影響に就て