クリープ破断ならびに高温疲労強度に及ぼす切欠きの影響
スポンサーリンク
概要
- 論文の詳細を見る
We have carried out creep rupture tests and high temperature fatigue tests for notched bars, to examine the general effect of notches on high temperature strength over prolonged periods of time. Test materials are ten kinds of heat resisting steels, ranging from low alloy steels to super alloys, and we have given them regular heat treatment in these tests. Notched specimens have U-type and V-type circumferential groove by machine cutting, which are respectively about 1.8 and 3 in stress concentration factor. The typical values of the above tests are tabulated in this report, with notch rupture strength ratio and strength reduction factor (β). Here, we obtained several conclusions as follows ; (1) The notch rupture strength ratio is generally larger than unity, as in the short time tensile test. But, it correlates closely with ductility variation of materials, depending on progressive precipitation and aging, with the increase of applied temperature and time. (2) Within the range of the tests, all the test points of ten materials have about the same correlation for the notch rupture strength ratio to the value of plain bar contraction, at corresponding rupture time, and it falls under unity when the plain bar is contracted below approximately 30% in V-notch, and 20% in U-notch. It is convenient to assume notch effect from plain bar creep rupture tests. (3) This ratio has a tendency to decrease after it has once increased, with the increase of notch sharpness. When in has large ductility the maximum value is high, but with small ductility, it gradually falls. (4) In general, the ratio for austenitic alloys is lower than for ferritic alloys. Particularly, 25-20 stainless steels showed the highest notch sensitivity of all the test materials. (5) Concerning the high temperature fatigue, there was a tendency in the strength reduction factor (β) for ferritic alloys to decrease, and for austenitic alloys to increase at high temperature.
- 社団法人日本材料学会の論文
- 1963-03-15
著者
関連論文
- 金属材料の高温疲労強度に関する研究
- 金属材料の重複繰返応力に対する疲労強度に関する研究 : 2段2重重複繰返応力に対する疲労強度
- 鋼構造物における溶接継手部の疲労強度推定
- 425 溶接継手の疲れ限度推定法
- SUS 316切欠き材の高温低サイクル疲労および破面に及ぼす保持時間の影響
- クリープ破断ならびに高温疲労強度に及ぼす切欠きの影響
- 各種耐熱鋼の高温疲労およびクリープ・ラプチャー強度
- 耐熱合金 Inconel 700 のクリープ破断強度と疲労強度に及ぼす高温腐食ふん囲気の影響
- カスタービン翼用耐熱合金の熱疲労強度に及ぼす材質の変化の影響
- 3次元破面解析技術FRASTA法の適用性に関する研究
- 黒鉛形状の定量的解析に基づく片状黒鉛鋳鉄の強度評価(フラクトグラフィ特集)
- 疲労破面粗さに基づく作用応力推定
- 高温水中における SUS 304 鋼の低サイクル疲労強度と破面
- 12. 事故解析 : フラクトグラフィと破壊力学
- クリープ試験機の試作と2,3の結果について
- 実働応力疲労に及ぼす負荷条件の影響と推定寿命 : 疲労限度以上の応力を少数回含む場合
- 「新しい工業材料」特集号発刊に際して
- 破壊事故および対策の最近の傾向 : (4)高温機器の環境による損傷と対策(破壊事故の解析と防止対策小特集号)
- ねじ継手におけるねじ山の弾塑性たわみとひずみ集中
- 鋼材の欠陥と疲労強度に関する一資料