変動応力下における繊維強化複合材料の疲労き裂伝ぱと損傷の進展

概要

論文の詳細を見る
Fatigue crack growth behavior of continuous fiber reinforced composite materials was studied under variable stress conditions. Two kinds of lminates with different ductility were employed : a hybrid laminate of glass fiber-reinforced epoxy and 7075-T6 aluminum alloy (Glare1) and a plainweave roving fabric laminate of glass fiber-reinforced epoxy (GFRP). Fatigue tests of center-notched (GRARE1) and double-edge-notched (GFRP) plate specimens were performed for the cases of stress-increase and stress-decrease, under repeated tension-tension and alternating tension-compression loading conditions. For GLARE1, acceleration and retardation of crack growth were observed under repeated tension-tension loading condition, while they were not under alternating tension-compression loading condition. The fatigue crack of this material propagated only in the aluminum layer, and its growth rate was not adequately correlated with the stress intensity factor range ΔK. It was found that the crack growth rate was successfully correlated with an effective stress intensity factor range ΔK_<eff> defined taking into account both the crack-closure and the fiber-bridging in the crack wake so that ΔK_<eff>=ΔK_<br>-ΔK_<cl>. The acceleration and retardation were explained using this parameter. For GFRP, on the other hand, no appreciable effect of the stress change on fatigue crack growth was detected. This was attributed to the brittleness of this laminate. The crack growth rate, in this case, was correlated well with the stress intensity factor range.
社団法人日本材料学会の論文
1993-01-15

変動応力下における繊維強化複合材料の疲労き裂伝ぱと損傷の進展

スポンサーリンク

概要

著者

関連論文

スポンサーリンク