低合金鋼の低温焼もどしぜい性の破壊力学的検討(<小特集>X線材料強度小特集)

概要

論文の詳細を見る
Tempered martensite embrittlement in low alloy steel was studied in terms of fracture toughness. The effects of plate thickness and notch root radius on crack initiation were analysed from a view point of fracture mechanics. The results obtained are summarized as follows: (1) The decrease in crack initiation stress intensity factor K_<init>~it for the fatigue precracked specimens under plane strain conditions corresponded to the degree of tempered martensite embrittlement. (2) The crack initiation stress intensity factor was correlated to the square root of the notch radius p^<1/2> for the thick specimens. Tempered martensite embrittlement appears in the crack initiation stress intensity factor K_<init> of the specimen having a large notch root radius and large thickness.