液体アンモニア処理木材の割裂破壊におけるAEの挙動
スポンサーリンク
概要
- 論文の詳細を見る
The acoustic emission (AE) signals associated with the cleavage fracture process were measured during fracture toughness tests of Sugi (Cryptomeria japonica) and Red lauan (Shorea negrosensis) woods. In addition, the effects of liquid ammonia treatment on the fracture toughness and the AE parameters such as event count, amplitude distribution and spectrum were examined. The following results were obtained ; The AE total count, NT under the tests up to the maximum load in Sugi was larger than that of Red lauan wood. For both woods, NT of radial direction (crack surface : TL plane) was larger than that of tangential direction (RL plane). After the liquid ammonia treatment, AE events were decreased considerably, and NT in Sugi and Red lauan were reduced to one fifth and half, respectively. From the AE amplitude distribution analysis, the difference in distribution profile between RL -and TL-cracking was observed in untreated Sugi, but not observed in treated Sugi, nor in treated and untreated Red lauan. The characteristics of AE spectra in TL and RL planes were examined, but any good result could not be obtained. The fracture toughness, G_<IC> of TL and RL planes in Red lauan were approximately 0.42 and 0.25 N/cm, respectively. After treating with liquid ammonia, G_<IC> was increased with the treatment time. The G_<IC> of TL plane had a constant value (1.43 N/cm) after 8 hours of the treatment, and the G_<IC> of RL plane took a maximum value (0.97 N/cm) at 15 hours.
- 社団法人日本材料学会の論文
- 1990-04-15
著者
関連論文
- アミノ基を有するジエンオリゴマ-の合成
- ナイロン6へのアニオングラフト重合
- 点ビ-ムを用いたX線小角散乱測定装置の製作
- X線用一次元位置敏感型比例計数管の製作
- 被服材料の教材研究(その2) : 撥水性繊維について(論文編)
- 2・3石低周波増幅器の設計とその応用 : (I) コレクタ電流の温度特性について
- 液体In-Hg, In-Bi, In-G, In-Sn合金の圧縮率
- VI-2.液体金属合金の音速-圧縮率の測定(『液体金属の構造と物性』,物性研短期研究会報告)
- 15.液体金属の密度,音速,圧縮率測定の問題点(「第2回液体金属の物性と構造に関する研究討論会」,研究会報告)
- 液体ビスマスの音速(液体金属の物性と構造に関する研究討論会(第1回)報告,研究会報告)
- 被服材料の教材研究(その1) : 吸水性繊維について(論文編)
- Velocity of Sound in Low Melting Liquid Metals
- 333 アコースティック・エミッション法による木材の割裂破壊の評価(コンクリート及び木材)
- 301 スギあて材の弾性および粘弾性変形挙動について(木質材料)
- 234 スギ材の飽水及び加熱下における曲げクリープ : 力学モデルによる遅延時間・弾性平衡の解析(木質材料の物性-II)(木材・木質材料の新展開 : ナノからメートルまで)(オーガナイスドセッション3)
- 液体アンモニア処理木材の割裂破壊におけるAEの挙動
- 木材の超音波伝播速度におよぼす繊維傾斜角の影響
- ピクノメーターによる液体金属の密度の連続測定法
- キチンの微粒子化 その3