純アルミニウムの疲労破損に及ぼす結晶粒径の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effect of grain size on fatigue damage in pure aluminium was studied in fully reversed plane bending by using the X-ray microbeam technique and optical microscopy. The results are summa-rized as follows : (1) The fatigue strength was found to be affected by the grain size in aluminium, although the substructure was well developed. This is interpreted on the basis that the crack initiation is affected by the grain size and the crack propagation takes place mostly along the grain boundary at higher stress amplitudes, but is retarded in the vicinity of the grain boundary at lower stress amplitudes. The grain size dependence of fatigue strength also seems to be associated with the purity of material. (2) The Petch's type relation did not exist between the fatigue strength and the grain size. The fatigue strength plotted against the inverse square root of grain size did not fall on a straight line but on a downwards bent line. This appears to have resulted from the facts that the stress amplitude at the transition from intergranular to transgranular cracking is also affected by the grain size as is the fatigue strength, and that the substructure develops more in the specimens having smaller grain sizes. (3) The subgrain size was found to be inversely proportional to the stress amplitude. But the subgrain size was also affected by the grain size and became smaller in the specimens with grains less than 50 /Im. On the other hand, both (D_b)_<max> and (D_b)_<min> increased with an increase of stress amplitude and, furthermore, the former increased a little with increasing grain size.
- 1977-03-15
著者
関連論文
- 溶接残留応力の固有ひずみ解析および熱弾塑性解析とその中性子回折測定による検証
- 多層溶接周継手における溶接順序が残留応力に及ぼす影響
- 複雑な形状をした溶接構造物における残留応力の簡易解析法
- 厚板を貫通する配管溶接部における残留応力の簡易弾性解析法の検討
- 集合組織を有するAl合金製嵌合継手の中性子回折による残留応力測定
- 中性子回折による炭素鋼配管突合せ溶接継手の残留応力(X線材料強度)
- 中性子回折によるソケット溶接継手の残留応力の測定
- 中性子回折による残留応力測定における弾性定数の回折面依存性(X線材料強度)
- オーステナイト系ステンレス鋼SUS 304の純水中における高サイクル熱疲労き裂発生挙動
- 純水中高サイクル熱疲労試験装置の開発と回転二重円筒隙間部の熱伝達率測定