浸炭材料の表面不完全焼入層の疲労挙動
スポンサーリンク
概要
- 論文の詳細を見る
The effect of the surface non-martensitic microstructure on the fatigue of gas carburized steel was investigated experimentally. The following results were obtained. (1) The fully reversed fatigue strength of carburized steel was lowered by the surface non-martensitic layer. (2) It was confirmed by X-ray stress measurements that the surface layer deformed plastically during the fatigue test and the residual stress developed in the direction to release the applied mean stress partially. (3) Scanning electron micrographs revealed that internal oxides act as the defects to initiate fatigue cracks. (4) The fatigue fracture mode of carburized steel was characterized by the transgranular fracture with a linear pattern along the direction of crack propagation.
- 社団法人日本材料学会の論文
- 1977-01-15
著者
関連論文
- 427 軟層継手を有する80Kg/mm^2級高張力鋼の疲労強度について
- 426 Mn-B系80Kg/mm^2級高張力鋼の溶接諸特性について
- 浸炭焼入材の疲労破面観察
- 高周波焼入材のねじり疲労強度
- 131 高周波焼入材のねじり疲労強度(疲労強度,セラミックス)
- 119 浸炭材の疲労挙動と破面形態(疲労破面)
- 3-32 引張り変形した鋼材料の半価幅と硬さの変化
- 1-17 浸炭材料の疲労強度におよぼす 1 次焼入れの影響
- 3-33 X 線応力測定側傾法による測定応力値について
- 1-22 浸炭材の疲労におよぼす熱処理の影響
- 低温における軟鋼切欠き材の破壊機構について
- 103 浸炭層の疲労き裂進展速度と破面様相
- 120 き裂進展に伴なう塑性変形域の X 線回折による解析
- 熱処理鋼の疲労破面の残留応力 (X線材料強度小特集)
- 122 熱処理鋼の疲労破面の残留応力
- 浸炭材料の表面不完全焼入層の疲労挙動
- 焼入焼きもどしされた鋼材料の半価幅とかたさの対応について
- 3-25 固溶硬化材と析出硬化材の半価幅と硬さの関係について
- (2-14) 過共析鋼の耐土砂摩耗性について
- 小松製作所・技術研究所・エンジン研究室
- 鋳鉄の熱疲労強度の研究
- B-9 脆性材料を使用した構造物の設計法
- 1-24 浸炭材料の疲労性質に関する研究 : 表面不完全焼入層の影響について