焼入焼きもどしされた鋼材料の半価幅とかたさの対応について
スポンサーリンク
概要
- 論文の詳細を見る
An investigation has been made on the relation between half value breadth (H. V. B.) and hardness of quenched-tempered steels. The following results have been obtained. (1) There are some good correlations between H. V. B. and hardness of quenched-tempered steels. These correlations are classified by the carbon content of steels and are well worth taking advantage for engineering use. (2) The change in H. V. B. is not influenced by precipitation hardening though it is remarkably affected by solid solution hardening and dislocation density. However. the change in hardness is not so remarkable as that in H. V. B. with dislocation density. (3) The result of tensile test revealed that H. V. B. having a value over 4.0 degree in 2θ decreases with plastic strain until the strain reaches at a certain value before it began to increase with strain, though H. V. B. under 4.0 degree increases monotonously with strain from the initial state.
- 社団法人日本材料学会の論文
- 1977-01-15
著者
関連論文
- 427 軟層継手を有する80Kg/mm^2級高張力鋼の疲労強度について
- 426 Mn-B系80Kg/mm^2級高張力鋼の溶接諸特性について
- 3-32 引張り変形した鋼材料の半価幅と硬さの変化
- 1-17 浸炭材料の疲労強度におよぼす 1 次焼入れの影響
- 3-33 X 線応力測定側傾法による測定応力値について
- 1-22 浸炭材の疲労におよぼす熱処理の影響
- 低温における軟鋼切欠き材の破壊機構について
- 154 小型試験によって鋼の低温靱性に関する基本値を求める研究(低温靱性, 加工・性質・分析, 日本鉄鋼協会 第 82 回(秋季)講演大会)
- 103 浸炭層の疲労き裂進展速度と破面様相
- 120 き裂進展に伴なう塑性変形域の X 線回折による解析
- 熱処理鋼の疲労破面の残留応力 (X線材料強度小特集)
- 122 熱処理鋼の疲労破面の残留応力
- 浸炭材料の表面不完全焼入層の疲労挙動
- 焼入焼きもどしされた鋼材料の半価幅とかたさの対応について
- 3-25 固溶硬化材と析出硬化材の半価幅と硬さの関係について
- (2-14) 過共析鋼の耐土砂摩耗性について
- 小松製作所・技術研究所・エンジン研究室
- 205 低温における鋼の切欠底下部組織に関する電顕観察(溶接・低温脆性・快削鋼, 加工・性質, 日本鉄鋼協会 第 83 回(春季)講演大会)
- 153 低温における鋼の切欠底下部組織に関する電顕観察(低温靱性, 加工・性質・分析, 日本鉄鋼協会 第 82 回(秋季)講演大会)